(100)[001] Secondary Recrystallization in Silicon Steel by “Low Vacuum” Annealing
نویسندگان
چکیده
منابع مشابه
Kinetics of Secondary Recrystallization in Grain-oriented Silicon Steel Studied by High-temperature Background
Secondary recrystallization id grain-oriented silicon steel is studied by the high-temperature background damping. Abnormal grain growth involves an abrupt drop of the background. The temperatures of initiation and completion of the secondary recrystallization are, thus, determined for the sane sample from the definite change in background with increasing temperature. The background measured on...
متن کاملSecondary recrystallization characteristics of 3%Si grain-oriented electrical steel
A secondary recrystallization Lab study focusing on the secondary recrystallization temperature and magnetic properties was carried out on cold rolling industrial samples of 3%Si grain-oriented electrical steel produced by low slab reheating temperature technology. The results showed a secondary recrystallization temperature, determined by the observed grain size change, of 1080 C with annealin...
متن کاملFormation of annealing twins during recrystallization and grain growth in 304L austenitic stainless steel
Understanding of the mechanisms of annealing twin formation is fundamental for grain boundary engineering. In this work, the formation of annealing twins in a 304L austenitic stainless steel is examined in relation to the thermo-mechanical history. The behavior of annealing twins of various morphologies is analyzed using an in-situ annealing device and EBSD. The results confirm that there is a ...
متن کاملRecrystallization of silicon by pulsed lasers
2014 Calculation of the evolution of temperature during pulsed laser annealing has been performed. The results are presented in directly useful figures for the two kinds of laser generally used (YAG, Ruby). The results are compared to various experimental measurements performed by RBS. If the crystallographic quality is quite good, TSC and DLTS measurements have shown that electrically active d...
متن کاملKinetics of Austenite Recrystallization during the Annealing of Cold-rolled Fe-Mn-Al-C Steel
In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Japan Institute of Metals
سال: 1962
ISSN: 0021-4434,2432-4701
DOI: 10.2320/matertrans1960.3.124