3D characterization of porosity in an air plasma-sprayed thermal barrier coating and its effect on thermal conductivity
نویسندگان
چکیده
منابع مشابه
High-temperature degradation of plasma sprayed thermal barrier coating systems
Thermal barrier coating systems (TBCs) are used in gas turbines to prevent high-temperature degradation of metallic materials in the combustor and turbine. One of the main concerns regarding TBCs is poor reliability, and accurate life prediction models are necessary in order to fully utilise the beneficial effects of TBCs. This research project aims at developing deeper understanding of the deg...
متن کاملThermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
The effects of the bond coat species on the delamination or fracture behavior in thermal barrier coatings (TBCs) was investigated using the yclic thermal fatigue and thermal-shock tests. The interface microstructures of each TBC showed a good condition without cracking or delamination after flame thermal fatigue (FTF) for 1429 cycles. The TBC with the bond coat prepared by the air-plasma spray ...
متن کاملThermal Conductivity Analysis and Lifetime Testing of Suspension Plasma-Sprayed Thermal Barrier Coatings
Suspension plasma spraying (SPS) has become an interesting method for the production of thermal barrier coatings for gas turbine components. The development of the SPS process has led to structures with segmented vertical cracks or column-like structures that can imitate strain-tolerant air plasma spraying (APS) or electron beam physical vapor deposition (EB-PVD) coatings. Additionally, SPS coa...
متن کاملThermal Conductivity of a Zirconia Thermal Barrier Coating
The conductivity of a thermal-barrier coating composed of atmospheric plasma sprayed 8 mass percent yttria partially stabilized zirconia has been measured. This coating was sprayed on a substrate of 410 stainless steel. An absolute, steady-state measurement method was used to measure thermal conductivity from 400 to 800 K. The thermal conductivity of the coating is 0.62 W/(m⋅K). This measuremen...
متن کاملAir Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading
An experimental investigation was conducted to find the effect of spraying method of coating of Thermal Barrier Coatings (TBCs) on their oxidation behaviour and resistance to various thermal loading. Isothermal and thermal shock tests were performed in order to study oxidation behaviour of air plasma sprayed Bond Coat (BC) and assess its effect on TBCs lifetime under the stated loadings. Specim...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the American Ceramic Society
سال: 2018
ISSN: 0002-7820
DOI: 10.1111/jace.15409