3D Printing and Performance of Continuous Fiber Reinforced Variable Stiffness Composite Structures
نویسندگان
چکیده
منابع مشابه
3d Printing with Natural Fiber Reinforced Filament
An initial study of 3d printing with compound filament using different plastic matrices and sugar cane bagasse as the filler was conducted. In order to do this, a reverse engineering process was made to several 3d printer extruders to determine how to change the extruder in order to be able to print with the filament. To obtain the filament, a plastic extruder was modified to obtain a compound ...
متن کامل3D Printing Variable Stiffness Foams Using Viscous Thread Instability
Additive manufacturing of cellular structures has numerous applications ranging from fabrication of biological scaffolds and medical implants, to mechanical weight reduction and control over mechanical properties. Various additive manufacturing processes have been used to produce open regular cellular structures limited only by the resolution of the printer. These efforts have focused on printi...
متن کاملThree-dimensional printing fiber reinforced hydrogel composites.
An additive manufacturing process that combines digital modeling and 3D printing was used to prepare fiber reinforced hydrogels in a single-step process. The composite materials were fabricated by selectively pattering a combination of alginate/acrylamide gel precursor solution and an epoxy based UV-curable adhesive (Emax 904 Gel-SC) with an extrusion printer. UV irradiation was used to cure th...
متن کاملUV-Assisted 3D Printing of Glass and Carbon Fiber-Reinforced Dual-Cure Polymer Composites
Glass (GFR) and carbon fiber-reinforced (CFR) dual-cure polymer composites fabricated by UV-assisted three-dimensional (UV-3D) printing are presented. The resin material combines an acrylic-based photocurable resin with a low temperature (140 °C) thermally-curable resin system based on bisphenol A diglycidyl ether as base component, an aliphatic anhydride (hexahydro-4-methylphthalic anhydride) ...
متن کاملFiber- Reinforced Composite for Orthodontic Anchorage Technique
Introduction: In orthodontic treatment, adequate anchorage is necessary to move the intended teeth. In some cases, just anterior teeth are malaligned, while posterior occlusion is acceptable. Therefore, the posterior teeth could be integrated by fiber-reinforced composite (FRC) to provide a rigid anchorage. This method proved advantageous since brackets are bonded just to anter...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Jixie gongcheng xuebao
سال: 2022
ISSN: ['0577-6686']
DOI: https://doi.org/10.3901/jme.2022.05.170