A method for evaluating subsurface damage in optical glass
نویسندگان
چکیده
منابع مشابه
Subsurface Damage in Microgrinding Optical Glasses
LLE Review, Volume 73 45 In cold processing of optical glasses by microgrinding,1,2 the resulting brittle-material-removal rate induces a cracked layer near the glass surface, referred to as subsurface damage (SSD). [Editor’s note: The acronym for subsurface damage (SSD) used in this article should not be confused with its more common use as an acronym for smoothing by spectral dispersion.] In ...
متن کاملA Method for Evaluating Glass Knives
In microtomy, faults of the cutting edge are an obvious and avoidable source of artifact. The purpose of this communication is to describe a simple apparatus for viewing and marking the cutting edge of the glass knives which are used in see-tioning for electron microscopy (1, 2). The apparatus consists of a monocular microscope with base, arm, body tube, coarse and fine adjustments, an annular ...
متن کاملA Cause of Damage to Optical Glass in the Tropics
Deterioration of the glass of microscope objectives, telescope lenses, prisms and expensive optical glass of all kinds has always been a source of worry to those using optical apparatus in the tropics. Many theories have been advanced to explain this damage, but as far as is known few, if any, of these have ever been definitely proved. In the present investigation, one cause of the clouding of ...
متن کاملExperimental Investigation of Subsurface Damages Made by Cup Grinding and Lapping Process of Optical Glass BK7 in Ductile Mode
Conventional material removal of BK7 optical glass will normally result in brittle fracture at the surface, generating severe subsurface damage and poor surface finish. Subsurface damages induced by grinding strongly influence the mechanical strength and optical quality of optical glasses. However, through ductile mode grinding it is possible to reduce the surface and subsurface cracks. It is m...
متن کاملExperimental Investigation of Subsurface Damages Made by Cup Grinding and Lapping Process of Optical Glass BK7 in Ductile Mode
Conventional material removal of BK7 optical glass will normally result in brittle fracture at the surface, generating severe subsurface damage and poor surface finish. Subsurface damages induced by grinding strongly influence the mechanical strength and optical quality of optical glasses. However, through ductile mode grinding it is possible to reduce the surface and subsurface cracks. It is m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Optics Express
سال: 2010
ISSN: 1094-4087
DOI: 10.1364/oe.18.017180