A Study on Fatigue Crack Growth Parameters for Fatigue Life Assessment based on Fracture Mechanics
نویسندگان
چکیده
منابع مشابه
The Fracture Mechanics Concept of Creep and Creep/Fatigue Crack Growth in Life Assessment
There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...
متن کاملSide Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملFretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life
Fretting fatigue experiments and finite element analysis were carried out to investigate the influence of cylindrical-on-flat contact on crack nucleation, crack path and fatigue life of medium-carbon steel. The location of crack nucleation was predicted using the maximum shear stress range criterion and the maximum relative slip amplitude criterion. The prediction using the maximum relative sli...
متن کاملFracture toughness and fatigue crack growth characteristics of nanotwinned copper
Recent studies have shown that nanotwinned copper (NT Cu) exhibits a combination of high strength and moderate ductility. However, most engineering and structural applications would also require materials to have superior fracture toughness and prolonged subcritical fatigue crack growth life. The current study investigates the effect of twin density on the crack initiation toughness and stable ...
متن کاملFracture Mechanics and Corrosion Fatigue
The development and current state-of-the-art in fracture mechanics in relation to studies of environment-enhanced fatigue-crack growth (corrosion fatigue) and fatigue-crack growth per se are reviewed. Patterns of response of materials to different loading and environmental conditions are considered in terms of the probable mechanisms for environmental embrittlement. The usefulness of the fractu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Welding and Joining
سال: 2017
ISSN: 2466-2232
DOI: 10.5781/jwj.2017.35.1.61