Hot Corrosion in Gas Turbines
DURING COMBUSTION in the gas turbine, sulfur from the fuel reacts with sodium chloride from ingested air at elevated temperatures to form sodium sulfate. The sodium sulfate then deposits on the hot-section components, such as nozzle guide vanes and rotor blades, resulting in accelerated oxidation (or sulfidation) attack. This is commonly referred to as “hot corrosion.” Sulfur in the fuel is gen...
متن کاملHot Corrosion of Slag Line in Plaster of Tundish in Continuous Casting of Steel
Plasters are produced from a light refractory material, mainly MgO (M.P. 2800ºC), a binder, and a void forming substance for insulating purposes. Different oxides from the slag penetrate into these voi...
متن کاملHot subdwarf stars in close-up view*
The origin of hot subdwarf B stars (sdBs) is still unclear. About half of the known sdBs are in close binary systems for which common envelope ejection is the most likely formation channel. Little is known about this dynamic phase of binary evolution. Since most of the known sdB systems are single-lined spectroscopic binaries, it is difficult to derive masses and unravel the companions’ nature,...
متن کاملAN INVESTIGATION ON EFFECT OF BOND COAT REPLACEMENT ON HOT CORROSION PROPERTIES OF THERMAL BARRIER COATINGS
In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING
سال: 1988
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1974.37.4_237