AAO-template assisted synthesis and size control of one-dimensional TiO2 nanomaterials
نویسندگان
چکیده
منابع مشابه
Facile Synthesis and Tensile Behavior of TiO2 One-Dimensional Nanostructures
High-yield synthesis of TiO(2) one-dimensional (1D) nanostructures was realized by a simple annealing of Ni-coated Ti grids in an argon atmosphere at 950 degrees C and 760 torr. The as-synthesized 1D nanostructures were single crystalline rutile TiO(2) with the preferred growth direction close to [210]. The growth of these nanostructures was enhanced by using catalytic materials, higher reactio...
متن کاملAAO-assisted synthesis of highly ordered, large-scale TiO2 nanowire arrays via sputtering and atomic layer deposition
Highly ordered nanoporous anodic aluminum oxide (AAO) thin films were fabricated in oxalic acid under a constant voltage via a two-step anodization process. To investigate the high-aspect-ratio (7.5:1) filling process, both sputtering and atomic layer deposition (ALD) were used to form TiO2 nanowires. Field emission scanning electron microscopy and high-resolution transmission electron microsco...
متن کاملNovel microwave assisted synthesis of ZnS nanomaterials.
A novel ambient pressure microwave assisted technique is developed in which silver and indium-modified ZnS is synthesized. The as-prepared ZnS is characterized by x-ray diffraction, UV-vis spectroscopy, x-ray photoelectron spectroscopy and luminescence spectroscopy. This procedure produced crystalline materials with particle sizes below 10 nm. The synthesis technique leads to defects in the cry...
متن کاملTemplate synthesis and characteristics of nanoparticle MgO
Oxide nanoparticles can exhibit unique physical and chemical properties due to their limited size and a high density of corner or edge surface sites. In this study, MgO nanoparticle was synthesized using Mg(CH3COO)2 and hexamethylenetetramine as starting materials. The structure and optical properties of these particles are investigated by using X-ray diffraction (XRD), sc...
متن کاملElectrodeposition of Single Crystalline Co56.48Ni43.52 Alloy Nanowires in AAO Template
Single crystalline cobalt nickel (Co-Ni) alloy nanowires are successfully fabricated using direct current (DC) electrodeposition with in the nanopore of highly ordered anodized aluminum oxide (AAO) template. SEM studies show that the average diameter of the alloy nanowires is approximately equal to 50 nm which corresponds to the pore size of the AAO template. Energy-dispersive X-ray (EDX) analy...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2013
ISSN: 1882-0743,1348-6535
DOI: 10.2109/jcersj2.121.915