Marginal Adaptation and Performance of Bioactive Dental Restorative Materials in Deciduous and Young Permanent Teeth
OBJECTIVE The aim of this study was to investigate the adaptation of different types of restorations towards deciduous and young permanent teeth. MATERIAL AND METHODS Class V cavities were prepared in deciduous and young permanent teeth and filled with different materials (a conventional glass-ionomer, a resin-modified glass-ionomer, a poly-acid-modified composite resin and a conventional com...
متن کاملa comparative analysis of the marginal microleakages of two pit and fissure sealans, conseal-f and conseal clear
چکیده ندارد.
15 صفحه اولEffect of Core Thickness and Porcelain Sintering on Marginal Adaptation
Background and aim: Marginal adaptation affects the long-term success of full-coverage restorations. This study aimed to assess the effect of porcelain sintering and zirconia core thickness on the marginal adaptation of all-ceramic restorations. Materials and methods: In this in-vitro experimental study, a standard brass die, 7 mm in length and 5 mm in diameter, was fabricated using a milling ...
متن کاملA Comparative Investigation of Marginal Adaptation and Surface Defects of MTA and Root MTA as Two Root End Filling Materials
Introduction: This study was carried out to compare two retrograde filling materials entitled mineral trioxide aggregate (MTA) and Root MTA (RMTA) in regard to their marginal adaptation and surface defects. Method: In this study twenty extracted human teeth were used. In all teeth after cleaning and shaping, the root canals were obturated by gutta-percha and root canal sealer. After that in eac...
متن کاملEffect of Thermocycling and Type of Restorative Material on Microleakage of Class II Restorations
Objectives: Microleakage is a major cause of failure of dental restorations and results in development of secondary caries, tooth hypersensitivity and pulp pathosis. This study aimed to compare the microleakage of class II cavities filled with two types of composite resins and a compomer and subjected to thermocycling. Methods: In this in vitro experimental study, class II cavities with a gi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Biomaterial Investigations in Dentistry
سال: 2019
ISSN: 2641-5275
DOI: 10.1080/26415275.2019.1696202