Adhesion of Chromium Electric-Spark Coatings on Steel Parts
نویسندگان
چکیده
منابع مشابه
08490 - Water Effects on Adhesion and Wear Resistance of Chromium Oxide Coatings
Nano-scratch and nano-indentation were used to determine hardness, elastic modulus, adhesion, friction and wear resistance of chromium oxide coatings in air and in water. The friction coefficient is higher in water, compared to air, and it increases with the applied normal load, although there are no obvious differences in hardness and elastic modulus in air vs. water. A higher normal load incr...
متن کاملPlasma spraying and characterization of chromium carbide – nickel chromium coatings
Chromium carbide – nickel chromium powder Cr3C2-25wt.NiCr was plasma sprayed by a water-stabilized system WSP®. A series of experiments with variable feeding distance was carried out. Basic characterization of coatings was done by XRD, SEM and light microscopy plus image analysis. Microhardness was measured on polished cross sections. The main focus of investigation was on resistances against w...
متن کاملThermal Stability of Phosphate Coatings on Steel
P. Pokorny, M. Novak, L. Mastny Institute of Chemical Technology, Prague, Czech Republic P. Szelag Pragochema Prague, Department of Research of Surface Treatment of Metals, Prague, Czech Republic V. Brozek Institute of Plasma Physics ASCR Prague, Czech Republic The work was validated thermal stability of zinc, manganese and tri-cations phosphate coatings on steel, made from commercial phosphati...
متن کاملPulsed plasma deposition of chromium oxide/chromium-cermet coatings
A novel radio frequency magnetron sputtering method for the deposition of composite films which consist of chromium oxide and chromium ~Cr2O3/Cr-cermet! is presented. As an extension to conventional reactive sputtering of a Cr target in an argon and oxygen atmosphere the oxygen flow into the process chamber is switched periodically on and off. This leads to an oscillating oxygen partial pressur...
متن کاملEffect of silica particles on adhesion strength of polyvinyl chloride coatings on metal substrates
The aim of this study was to improve the adhesion performance of plasticized polyvinyl chloride (PVC) coatings on steel substrates by using nanoparticles. For this purpose, the PVC plastisol with different concentration of nano-silica was prepared and applied to bond steel joints. The adhesive strength of the joints was determined by single-lap shear test. Moreover, mechanical properties and mi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallofizika I Noveishie Tekhnologii
سال: 2023
ISSN: ['1024-1809', '2617-1511']
DOI: https://doi.org/10.15407/mfint.45.01.0045