AE Measurements and Fracture Toughness Evaluation in Indentation Test for Alumina Ceramics
نویسندگان
چکیده
منابع مشابه
Fracture toughness measurement of dental ceramics using the indentation fracture method with different formulas.
This study examined fracture toughness (KIC) measurements obtained using the indentation fracture (IF) method with a view to improving their reliability. The KIC values of five dental ceramics were measured using the IF method with five different formulas, and the single-edge precracked beam (SEPB) method was used as a control. The elastic moduli of the dental ceramics were evaluated by dynamic...
متن کاملFracture Toughness of Ceramics by the Vickers Indentation Crack Length Method: a Critical Review
Fracture toughness is an important property that characterizes a material’s brittleness or resistance to fracture. Although some fracture toughness test methods have been refined and even standardized, many researchers have continued to use the Vickers indentation crack length method as an expedient. In this paper, Vickers indentation fracture resistance data for Standard Reference Material SRM...
متن کاملStatistical Analysis of Vickers Indentation Fracture Toughness of Y-tzp Ceramics
The purpose of this study was to investigate and analyse the fracture toughness of yttria stabilized tetragonal zirconia polycrystal (Y-TZP) dental ceramics by means of the Vickers indentation technique. Fracture toughness was analysed under the following loads: 29.42 N, 49.03 N, 196.13 N, and 294.20 N. Cracks that had developed from the vertices of a Vickers indentation were measured and used ...
متن کاملSimplified method for determining fracture toughness of two dental ceramics.
This study compared the fracture toughness values (KIC), which were derived from simplified techniques: the indentation fracture (IF), the indentation strength (IS), and fractographic approach to that from a standard testing using surface cracks in flexure (SCF). Forty bar specimens, twenty IPS Empress(®) Esthetic and twenty IPS e.max(®)Ceram were prepared. Ten specimens in each material were t...
متن کاملFracture toughness and thermal shock of tool and turbine ceramics
The behaviour of some commercial tool carbides and turbine ceramics has been investigated in regard to resistance to crack initiation, crack propagation and retained strength after thermal shock. New data are provided, particularly measurements of the fracture toughness of these materials at actual operating temperatures (up to 1200 ~ C). Many of the materials did not follow the generally accep...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1984
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.50.495