Age-precipitation in Al2O3 particle/Al-Cu alloy and SiC particle/Al-Cu-Mg alloy composite materials.

Precipitation Behavior and Quenching Sensitivity of a Spray Deposited Al-Zn-Mg-Cu-Zr Alloy

Precipitation behavior and the quenching sensitivity of a spray deposited Al-Zn-Mg-Cu-Zr alloy during isothermal heat treatment have been studied systematically. Results demonstrate that both the hardness and the ultimate tensile strength of the studied alloy decreased with the isothermal treatment time at certain temperatures. More notably, the hardness decreases rapidly after the isothermal h...

Dsc Study of Precipitation in an Al-mg-mn Alloy Microalloyed with Cu

Power compensation DSC has been employed to detect and analyse precipitation reactions in an Al1.3Mg-0.4Mn and an Al-1.3Mg-0.4Mn-0.07Cu alloy in which very small amounts of precipitate, less than 0.3 at%, are expected to form. Due to the very small heat effects, baseline instability and drift significantly interfere with the measurements. After repeated experiments and careful baseline correcti...

CORROSION BEHAVIOUR OF Al-Li-Cu-Mg ALLOY 8090-T651

Precipitation of a new platelet phase during the quenching of an Al-Zn-Mg-Cu alloy.

A previously undescribed high aspect ratio strengthening platelet phase, herein named the Y-phase, has been identified in a commercial Al-Zn-Mg-Cu alloy. Differential scanning calorimetry indicates that this phase only precipitates at temperature and cooling rate of about 150-250 °C and 0.05-300 K/s, respectively. This precipitate is shown to be responsible for a noticeable improvement in mecha...

TEXTURE AND RESISTIVITY OF Cu and DILUTE Cu ALLOY FILMS

Annealing of dilute binary Cu(Ti), Cu(In), Cu(Al), Cu(Sn), Cu(Mg), Cu(Nb), Cu(B), Cu(Co) and Cu(Ag) alloy films resulted in the strongest <111> fiber texture for Cu(Ti) and the lowest resistivity for Cu(Ag). The behavior of the alloy films was compared and contrasted with that for a pure evaporated Cu film. Electron beam evaporated films with compositions in the range of 2.0-4.2 at% and thickne...