Algorithm for automatic fatigue crack growth simulation on welded high strength steels
نویسندگان
چکیده
منابع مشابه
High-Strength Bainitic Steels
With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...
متن کاملHigh-temperature Fatigue Crack Growth Behavior of 17-4 Ph Stainless Steels
The fatigue crack growth (FCG) behavior was investigated for 17-4 PH stainless steels in three heat-treated conditions, i.e., unaged (Condition A), peak-aged (Condition H900), and overaged (Condition H1150), at temperatures ranging from 300 to 500 C. The high-temperature fatigue crack growth rates (FCGRs) of Condition H1150 were increased with an increase in temperature. However, for Conditions...
متن کاملFatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملEffect of heat input on the mechanical properties of welded joints in high-strength steels
Taylor & Francis makes every effort to ensure the accuracy of all the information (the “Content”) contained in the publications on our platform. However, Taylor & Francis, our agents, and our licensors make no representations or warranties whatsoever as to the accuracy, completeness, or suitability for any purpose of the Content. Any opinions and views expressed in this publication are the opin...
متن کاملThe Fatigue Strength of Fillet Welded Connections
This report describes a study of the fatigue behavior of fillet welded joints stressed perpendicular to the weld line. The study included an experimental phase in which the stiess-life and cracking behavior of load and nonload carrying fillet weld joints was determined. This experimental study concentrated on the fatigue behavior in the transition region between high and low cycle fatigue 3 5 (...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frattura ed Integrità Strutturale
سال: 2019
ISSN: 1971-8993
DOI: 10.3221/igf-esis.48.27