Annealing Effect of Glancing Angle Electron Beam Deposited TiO2/In2O3 Nanowires Array on Surface Wettability
نویسندگان
چکیده
منابع مشابه
Transport Properties of Beam-Deposited Pt Nanowires
Pt wires were fabricated by using electron-beam (EB) and Ga focused-ion-beam (FIB) irradiation while providing C5H5Pt(CH3)3 gas through a nozzle. Electron transport properties of the wires were investigated. The resistance of the EB-deposited wires was quite high as deposited but was reduced by 3–4 orders of magnitude after 400–500C annealing. The electron transport of the as-deposited EB-depos...
متن کاملEffect of annealing temperature on wettability of TiO2 nanotube array films
Highly ordered TiO2 nanotube array (TN) films were prepared by anodization of titanium foil in a mixed electrolyte solution of glycerin and NH4F and then annealed at 200°C, 400°C, 600°C, and 800°C, respectively. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), water contact angle (WCA), and photoluminescence (PL). It was found that low temperature (...
متن کاملStrong light coupling effect for a glancing-deposited silver nanorod array in the Kretschmann configuration
In this work, three slanted silver nanorod arrays (NRAs) with different thicknesses are fabricated using the glancing angle deposition method. Each silver NRA in the Kretschmann configuration is arranged to form a prism/NRA/air system. Attenuated total reflection occurs over the visible wavelengths and wide incident angles of both s- and p-polarization states. The extinctance is inversely propo...
متن کاملCharacterisation of electron-beam deposited tungsten interconnects
Electron beam deposition of tungsten from W(CO)6 has been studied for a range of different height deposits. The resistance of the deposited tracks was found to decrease with increasing height implying that thicker deposits have a higher metallic cross section. It was also found that when the current limits were increased to values in excess of 100 μA, the resistance decreased with successive vo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2020
ISSN: 2045-2322
DOI: 10.1038/s41598-020-66150-2