Application of β-Wollastonite on Bulk Density and Ignition Loss of Clay-Based Ceramic Materials

This work focuses on the effect of β-wollastonite percentage with different particle sizes bulk density and weight loss clay-based ceramics. The ceramic bodies were prepared by mixing clay a synthesized (5%, 15%, 25%) using solid slip casting method. (75 µm) (63, 75, 125 mixed fired at 950°C, 1000°C, 1050°C firing temperatures. fabricated material exhibited maximum 2.35 g/cm3 25% content β-wollastonite, 63 µm size temperature. However, minimum 1.87 was found 950°C A 2.32% ignition recorded specimen that contained In contrast, 4.37% observed body made up 5% 1050°C. general, result shows temperature, β–wollastonite, addition β–wollastonite have great materials.