Assessment of Corrosive Behaviour and Microstructure Characterization of Hybrid Friction Stir Welded Martensitic Stainless Steel
نویسندگان
چکیده
Abstract This study examined the effect of induction heating on microstructure and corrosion characteristics hybrid friction stir welded AISI 410 stainless steel. Five joints have been produced with different welding parameters like speed, spindle plunge depth, power. Their microstructures were evaluated using a scanning electron microscope, chemical composition was energy-dispersive X-ray spectroscopy (EDX). The rate found out via weight loss method in 1 M HCL solution. used for this work is assisted welding; results show that could produce sound steel Joints. experiment joint made at speed 1150 rpm, 40 mm/min, depth 0.5 mm, in-situ heat by 480°C better resistance property fine grain structure.
منابع مشابه
Evaluation of microstructure and mechanical properties of friction stir welded copper / 316L stainless steel dissimilar metals
In the present research, friction stir welding (FSW) process was used for butt joining of pure copper plate to 316L stainless steel plate. Mechanical properties and microstructural characteristics of the joint were evaluated by microhardness and tensile tests as well as optical and scanning electron microscope (SEM). It was found that microstructure of the weld nugget (WN) has fine grains where...
متن کاملMicrostructure, Mechanical and Corrosion Properties of Friction Stir Welding High Nitrogen Martensitic Stainless Steel 30Cr15Mo1N
High nitrogen martensitic stainless steel 30Cr15Mo1N plates were successfully welded by friction stir welding (FSW) at a tool rotation speed of 300 rpm with a welding speed of 100 mm/min, using W-Re tool. The sound joint with no significant nitrogen loss was successfully produced. Microstructure, mechanical and corrosion properties of an FSW joint were investigated. The results suggest that the...
متن کاملevaluation of microstructure and mechanical properties of friction stir welded copper / 316l stainless steel dissimilar metals
in the present research, friction stir welding (fsw) process was used for butt joining of pure copper plate to 316l stainless steel plate. mechanical properties and microstructural characteristics of the joint were evaluated by microhardness and tensile tests as well as optical and scanning electron microscope (sem). it was found that microstructure of the weld nugget (wn) has fine grains where...
متن کاملEffects of Friction Stir Processing on the Microstructure and Mechanical Properties of Fusion Welded 304L Stainless Steel
A variation of FSW, friction stir processing (FSP), has been used to modify selected regions of materials to enhance specific properties while eliminating fusion welding defects such as porosity, cracking, and the cast microstructure. The combination of fusion welding defects and high tensile residual stresses caused by the solidification of the molten weld pool adversely affect the post weld s...
متن کاملInfluence of rotational speed on the development of microstructure in a friction stir welded 304 austenitic stainless steel
Friction stir welding was conducted on AISI 304 austenitic stainless steel sheet with dimensions of 100 mm × 100 mm × 2 mm. The FSW was performed at a welding speed of 150 mm/min and rotational speeds of 400 and 800 rpm. The results showed that high frequency of low angle grain boundaries (LAGBs) were formed through dynamic recovery in the thermo-mechanically affected zone (TMAZ). Higher amoun...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advances in Materials Sciences
سال: 2021
ISSN: ['1730-2439', '2083-4799']
DOI: https://doi.org/10.2478/adms-2021-0025