Bainitic Transformation in View of Displacive Mechanism
نویسندگان
چکیده
منابع مشابه
NEW BAINITIC STEELS BY DESIGN Displacive Phase Transformations
Bainitic steels are now at the forefront of new and exciting developments in steel technology. This paper discusses how phase transformation theory is being exploited in the systematic design of every aspect of the new alloys, emphasising the immense influence that Professor Wayman has had on the development of the subject [1]. Technology of Bainitic Steels Gone are the days when industry could...
متن کاملStrong Bainitic Steels by Continuous Cooling Transformation
Using metallurgical models, three steels were designed to obtain carbide-free bainitic structures in the as-rolled condition. Experimental castings were hot-rolled in a pilot mill and their austenite decomposition kinetics were measured using dilatometry. Tensile and Charpy impact properties were measured and the microstructures were characterised using X-ray diffractometry, optical and scannin...
متن کاملStructural Mechanism of Close-Packed Polytypes Formation at Displacive Type Phase Transformation in Alloys
Statistics of one-dimensional disordering of polytypes formed under phase transformation of a displacive type of Co-alloys was studied. Discovered polytypes with a short-range order in close-packed atomic layers allowed to propose a mechanism of their formation by noncoherent displacements in the initial polymorphous modification along close-packed planes. Significant dependence of polytype str...
متن کاملMechanism of Bainite Transformation in Fe-Cr-Mo-V-Ti-C Steel
The kinetics and mechanism of bainite transformation have been studied in Fe-Cr-Mo-V-Ti-C steel high speed dilatometry backed by thermodynamic analysis. The complete transformation of austenite, however, has not occurred at any reported temperature. Obtained results confirm the incomplete reaction phenomenon with the cessation of the bainite transformation well before the paraequilibrium is ach...
متن کاملSolute Trapped at Defects during the Displacive Formation of Bainitic Ferrite
New developments with bainite have resulted in a steel with an ultimate tensile strength of 2500 MPa, a hardness of 600-670 HV and a toughness in excess of 30-40 MPa m [1]. The novel microstructure is generated in a high carbon (0.98 wt.%) high silicon (1.46 wt.%) steel austenitized for 15 min. at 1000 oC, and then isothermally transformed at temperatures of ∼200 oC. Iron does not diffuse durin...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Transactions, JIM
سال: 1991
ISSN: 0916-1821,2432-471X
DOI: 10.2320/matertrans1989.32.631