Behavior of G.P.Zone and Nucleation of Intermediate Precipitate in Al-Mg-Zn, Al-Mg-Zn-Cu Alloys
نویسندگان
چکیده
منابع مشابه
CORROSION FATIGUE CRACK PROPAGATION AND INHIBITION IN Al-Zn-Mg-Cu VS Al-Cu-Mg/Li ALLOYS
Age-hardenable aluminum alloys used in aerospace structures are susceptible to environment assisted fatigue crack propagation (EFCP), limiting component durability and safety. The objective is to quantitatively understand EFCP and its inhibition for important aerospace alloys: 7075-T651 (Al-Zn-Cu-Mg), C433-T3 (Al-Cu-Mg), and C47A-T86 (AlCu-Li). EFCP is understood through the hydrogen embrittlem...
متن کاملIn Vitro Degradation Behavior of Ternary Mg-Zn-Se and Mg-Zn-Cu Alloys as Biomaterials.
In this study, the corrosion behavior of Mg-Zn-Se and Mg-Zn-Cu alloys was investigated to evaluate their corrosion behavior related to use as implantable biomaterials. The corrosion behavior of these alloys and a commercially available Mg-Zn alloy were examined using static solution electrochemical testing, dynamic solution gravimetric testing, ion leaching testing, and microscopic evaluation. ...
متن کاملCORROSION BEHAVIOR OF THE Al-Zn-Mg-Cu ALLOYS WITH NICKEL ADDITIONS
In this research, comparative study of corrosion resistance of aluminum based alloys and Al-alloys with nickel have been investigated. Several processes are conducted for the AlZn-Mg-Cu alloys and Al-Zn-Mg-Cu-0.5%Ni alloys were homogenized, aged then retrogressed and reaged; also, alloys were homogenized then the extruded thereafter heat treated. Al-Zn-Mg-Cu alloy and AlZn-Mg-Cu-Ni alloy sample...
متن کاملQuench Rate Effects on the Natural Aging Behavior of 7xxx Al-mg-zn-cu Aluminum Alloys
The effect of quench rate on the natural aging behavior was examined using microhardness, conductivity and the differential scanning calorimeter. The data indicated that GPZ formed during extended natural aging of 7075, while extended aging of 7050 resulted in the precipitation of η’. Introduction The aluminum alloy system Al-Zn-Mg-Cu is the mainstay of aluminum alloys used in the aerospace ind...
متن کاملA model for the electrical conductivity of peak aged and overaged Al-Zn-Mg-Cu Alloys
A physically-based model for the electrical conductivity of peak aged and overaged Al-Zn-Mg-Cu (7xxx series) alloys is presented. The model includes calculations of the η and the S phase solvus (using a regular solution model), taking account of the capillary effect and η coarsening. It takes account of the conductivity of grains (incorporating dissolved alloying elements, undissolved particles...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1973
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.37.6_658