Behavior of mechanical alloying in metal-silicon systems.
نویسندگان
چکیده
منابع مشابه
Mechanical behavior of electrochemically lithiated silicon
The time-independent and time-dependent mechanical behavior of electrochemically lithiated silicon was studied with nanoindentation. As indentation was performed with continuous stiffness measurements during loading and load-hold, new insight into the deformation behavior of lithiated silicon is furnished. Supporting other research, Young's modulus and the hardness of lithiated silicon are foun...
متن کاملBehavior of Cu-Cr Powder Mixtures During Mechanical Alloying (TECHNICAL NOTE)
In the present work, the behavior of Cu-Cr powder mixtures during mechanical alloying has been studied. The powder mixtures with 1, 3 and 6 weight percents of Cr in Cu were treated. They were milled in a ball mill with two different speeds of 250 and 500 rpm using equal numbers of 1 and 2 centimeters balls. The weight ratio of balls to powders was 10 to 1 under argon atmosphere. Ethanol was use...
متن کاملRaney-nickel Catalysts Produced by Mechanical Alloying
Raney catalysts were prepared by a combination of mechanical alloying and leaching as an alternative in the synthesis of Raney-Nickel catalysts. Binary Al-Ni and ternary Al-Ni-Fe alloys with nominal compositions Al65Ni35, Al75Ni25, Al65Ni30Fe5, Al75Ni20Fe5 (in atomic percent), were processed from pure elemental powders; they consisted mainly of the intermetallic B2 AlNi phase. Aluminum was sele...
متن کاملInfluence of Alloying Treatment and Rapid Solidification on the Degradation Behavior and Mechanical Properties of Mg
Magnesium (Mg) has drawn increasing attention as a tissue engineering material. However, there have been very few studies of laser-melted Mg-Zn alloys. In this study, four binary Mg-xZn (x = 2, 4, 6 and 8 wt. %) alloys were fabricated by laser melting. The influence of zinc (Zn) content and technique on the degradation behavior and mechanical properties of Mg were discussed. Results revealed th...
متن کاملNickel aluminide containing refractory-metal dispersoids: 1: Synthesis by reactive mechanical alloying
Nickel and aluminum powders were mechanically alloyed with 10 or 30 vol.% refractory metal powders (molybdenum or tungsten) for times up to 50 h. Intermetallic synthesis takes place after lo-20 h alloying, with concomitant dispersion of the inert refractory metal phase, resulting in an NiAl matrix containing fine refractory dispersoids. The reactive synthesis step is direct, without intermediat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1990
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.37.652