Bending Properties of Nanocrystalline Ni-18 at% W Alloy Produced by Electrodeposition
نویسندگان
چکیده
منابع مشابه
HIGH-STRENGTH NANOCRYSTALLINE Ni-W ALLOYS PRODUCED BY ELECTRODEPOSITION
Nanocrystalline Ni-W alloys having both high ductility and high strength were produced by electrodeoisition. The plating bath for the electrodeposition contained nickel sulfate, citric acid, sodium tungstate and ammonium chloride, and was operated at various bath concentrations and conditions of electrolysis. The ductility and tensile strength of the deposited alloys are strongly influenced by ...
متن کاملPreparation of Ni-Co Alloy Foils by Electrodeposition
Electrodeposition of Ni-Co alloy foils on titanium substrate was performed in an acid chloride-sulphate bath. The influences of electrodeposition parameters such as current density, temperature, pH value, cobalt sulphate and saccharin concentration on composition and current efficiency were investigated in detail. The morphology and the microstructure of deposits were analyzed by SEM and XRD, r...
متن کاملHot Nanoindentation of Nanocrystalline Ni-W Alloys
High temperature nanoindentation experiments are conducted to assess the activation enthalpy for deformation of nanocrystalline Ni-W alloys, for grain sizes between 3 and 80 nm. Thermal softening becomes less pronounced at finer grain sizes, and the activation enthalpy has an apparent inflection at a grain size near ~10-20 nm, in the vicinity the Hall-Petch breakdown. This inflection is related...
متن کاملNanoindentation and micro-mechanical fracture toughness of electrodeposited nanocrystalline Ni–W alloy films
متن کامل
Wear behavior of carbon steel electrodeposited by nanocrystalline Ni–W coating
Ni-W coatings, compared to pure nanocrystalline Ni, exhibit higher hardness and wear resistance. In some cases, these coatings are considered as environmental friendly alternatives for hard chromium coating. Till now, most of Ni-W coatings have been produced by direct current electrodeposition from alkaline baths. In this study square pulse current was used for deposition of Ni-W precipitates f...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2004
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.45.1807