Biocompatibility of NiTi alloy implants in vivo
نویسندگان
چکیده
منابع مشابه
Biocompatibility of NiTi Alloy Implants in vivo
In this study, the powders of Ni and Ti with 50.5 at.% Ni for 12 h were blended and cold pressed at the different pressures (50, 75 and100 MPa).The porous product obtained after Ni-Ti compacts were synthesized by SHS (self-propagating hightemperature synthesis) in the different preheating temperatures (200, 250 and 300oC) and heating rates (30, 60 and 90oC/min). The effects of the pressure, pre...
متن کاملBiocompatibility of magnesium-zinc alloy in biodegradable orthopedic implants.
In this study, magnesium-zinc (Mg-Zn) alloy was investigated as a biodegradable orthopedic implant. MC3T3-E1 cell attachment, mineralization and osteogenic-specific mRNA expression were assessed for as measurements of the in vitro biocompatibility of Mg-Zn alloy. In vivo degradation of the Mg-Zn alloy and the accompanying new bone formation in the femoral marrow cavity were analyzed by scanning...
متن کاملIn vivo biocompatibility of three potential intraperitoneal implants.
The intraperitoneal biocompatibility of PDMS, polyHEMA and pEVA was investigated in rats, rabbits and rhesus monkeys. No inflammation was evidenced by hematological analyses and measurement of inflammatory markers throughout the experiment and by post-mortem examination of the pelvic cavity. After 3 or 6 months, histological analysis revealed fibrous tissue encapsulating PDMS and PEVA implants ...
متن کاملNanofretting behaviors of NiTi shape memory alloy
Nanofretting behaviors of NiTi shape memory alloy Linmao Qian a, Zhongrong Zhou a,∗, Qingping Sun b, Wenyi Yan c a Tribology Research Institute, National Traction Power Laboratory, Southwest Jiaotong University, Chengdu 610031, China b Department of Mechanical Engineering, The Hong Kong University of Science and Technology, Hong Kong, China c School of Engineering and Information Technology, De...
متن کاملMicrostructural characteristics and biocompatibility of a Type-B carbonated hydroxyapatite coating deposited on NiTi shape memory alloy.
Microstructural characteristics and biocompatibility of a Type-B carbonated hydroxyapatite (HA) coating prepared on NiTi SMA by biomimetic deposition were characterized using XRD, SEM, XPS, FTIR and in vitro studies including hemolysis test, MTT cytotoxicity test and fibroblasts cytocompatibility test. It is found CO(3)(2-) groups were present as substitution of PO(4)(3-) anions in HA crystal l...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Current Opinion in Biotechnology
سال: 2013
ISSN: 0958-1669
DOI: 10.1016/j.copbio.2013.05.105