Biodegradation of gelatin-g-poly(methyl acrylate)
نویسندگان
چکیده
منابع مشابه
Biodegradation of Gelatin-g-Poly( ethyl Acrylate)
Synopsis Gelatin-g-poly(ethy1 acrylate) copolymers were prepared in an aqueous medium, using KzS20~ initiator. The composition of the graft copolymers was dependent upon temperature and duration of the reaction. The number of grafting sites was small and molecular weight of the grafted poly(ethy1 acrylate) branches was high. Three copolymer samples with grafting efficiencies of 33.3% 61.0%, and...
متن کاملSynthesis, characterization and swelling behavior investigation of gelatin-g-Poly(Acrylic Acid-co-Itaconic Acid)
A novel pH-responsive superabsorbent hydrogel based on gelatin was prepared through crosslinking copolymerization of poly (acrylic acid) and poly (itaconic acid). The copolymerization conditions including monomers, initiator, gelatin and crosslinker concentration, reaction temperature, and neutralization percent were systematically optimized to achieve a hydrogel with swelling capacity as high ...
متن کاملInsertion polymerization of acrylate.
Multiple insertions of acrylate in copolymerization with ethylene, and an insertion homo-oligomerization of methyl acrylate were observed for the first time. Key to these findings, and to mechanistic insights reported, are labile-substituted complexes as catalyst precursors.
متن کاملSynthesis and thermal characterization of polymethyl methacrylate
PMMA with molecular mass (PMMA Mw: 1.2×105) was synthesized through AIBN initiated free radical polymerization methyl methacrylate at 100 ± 1°C.The synthesized polymer was characterized through GPC coupled with RI detector in presence of THF as mobile phase at 1.0 mL/ min and simultaneous TG-DTA-DTG in nitrogen. TG data were used to investigate the non-isothermal kinetics of solid-state decompo...
متن کاملn-Butyl acrylate.
1.1.3 Chemical and physical properties of the pure substance From American Conference of Governmental Industrial Hygienists (1991) unless otherwise noted. (a) Description: Colourless, flammable liquid (b) Boiling-point: 145°C (Lide, 1997) (c) Melting-point: –64.6°C (Lide, 1997) (d) Solubility: Very slightly soluble in water (0.14% at 20°C); soluble in ethanol, diethyl ether and acetone (e) Vapo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Polymer Science: Polymer Chemistry Edition
سال: 1981
ISSN: 0360-6376,1542-9369
DOI: 10.1002/pol.1981.170190522