Bridged interface cracks under transient thermal loading

نویسندگان

چکیده

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Bridged interface cracks in anisotropic bimaterials

The bonding strength between dissimilar materials in composites is often relatively weak. Interface debonding and cracking are of common occurrence. As an e€ ective method to minimize such failures, ® bre stitching is used to enhance the bonding strength when joining layers in polymer composites. With the presence of the reinforcing ® bre, the overall elastic response for each component of the ...

متن کامل

Thermal resistance of bridged cracks in fiber-reinforced ceramic composites

The thermal resistance of a bridged matrix crack in a fiber-reinforced ceramic composite is analyzed. The problem is cast in terms of a unit cell comprising an infinitely long composite cylinder with a single matrix crack perpendicular to the fiber axis. At the outset, it is demonstrated that the thermal resistance of such a crack can be represented by a simple circuit consisting of two paralle...

متن کامل

Interface Cracks

-Properties of elastic solutions to interface crack problems are discussed in both the open formulation, in which the crack faces are assumed to be traction-free and interpenetration is permitted, and the unilateral formulation, where a contact zone is generally established adjacent to the crack tips. It is shown that if the contact zone is sufficiently small compared with the other dimensions ...

متن کامل

Stress Analysis Near the Welding Interface Edges of a QFP Structure under Thermal Loading

The purpose of this paper was to investigate the reason why the interface delaminations occurred in the QFP structure. The stress concentration was the key factor responsible for the microcrack occurrence. In order to figure out which factors affect the stress distribution, the material’s attributes and the structure’s dimension were considered. The finite element program ABAQUS6.9 together wit...

متن کامل

Exterior Interface Cracks

Abstract-Continuing a recent investigation of interface cracks, attention is paid to the exterior crack. Two elastic solids bonded over a finite segment of their boundary and capable of transmitting shear and tensile tractions are considered. It is found that one of the edge cracks remains completely closed under shear alone, and opens gradually as the level of tension is increased. Both crack ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: PAMM

سال: 2007

ISSN: 1617-7061,1617-7061

DOI: 10.1002/pamm.200700848