Carbothermic reduction of mechanically activated NiO-carbon mixture: Non-isothermal kinetics
نویسندگان
چکیده
منابع مشابه
The effect of mechanical activation on the carbothermic reduction kinetics of hematite-graphite mixture
The effect of mechanical activation on structural changes and kinetics of carbothermic reduction of hematite with graphite was studied in this research. Hematite powder mixture with graphite (with stoichiometry ratio C/O=1) was milled for the time periods of zero to 50 hours, and the structural changes were studied using X ray diffraction (XRD). The effect of mechanical activation on the kineti...
متن کاملKINETICS OF CARBOTHERMIC REDUCTION OF AN IRANIAN CELESTITE ORE
Two commercial methods are used for the production of strontium carbonate:1) Direct conversion of Celsetite to strontium carbonate by hot sodium carbonate,2) Carbothermic reduction of celestite with coal followed by water leaching of strontium sulfide(SrS) and its conversion to strontium carbonate.The present study has been made on the carbothermic reduction of celestite ores of Varamin (Iran) ...
متن کاملthe effect of mechanical activation on the carbothermic reduction kinetics of hematite-graphite mixture
the effect of mechanical activation on structural changes and kinetics of carbothermic reduction of hematite with graphite was studied in this research. hematite powder mixture with graphite (with stoichiometry ratio c/o=1) was milled for the time periods of zero to 50 hours, and the structural changes were studied using x ray diffraction (xrd). the effect of mechanical activation on the kineti...
متن کاملNon-Isothermal Dehydration Kinetics of Diphasic Mullite Precursor Gel
Aluminosilicate gel precursor having mullite composition was synthesized from inorganic salts of aluminum and silicon by employing the sol-gel method. Chemical analysis, surface area and bulk density measurements were performed to characterize the dried gel. The course of the mullitization was examined by FT-IR analysis which confirmed the diphasic nature of the gel. ...
متن کاملNon-isothermal Primary Crystallization Kinetics of the Amorphous Fe85.3B11P3Cu0.7 Alloy
In the present research, the primary crystallization kinetics of the amorphous Fe85.3B11P3Cu0.7 alloy was analyzed using non-isothermal DSC measurements. The average and local activation energies, Ea, were determined by different isokinetic and isoconversional methods. The results obtained for activation energy in this research, show that due to the complexity of the primary crystallization pro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Mining and Metallurgy, Section B: Metallurgy
سال: 2018
ISSN: 1450-5339,2217-7175
DOI: 10.2298/jmmb180323022b