Characteristic of Bamboo Particleboard Bonded with Citric Acid
نویسندگان
چکیده
منابع مشابه
Low Density Sugarcane Bagasse Particleboard Bonded with Citric Acid and Sucrose: Effect of board density and additive content
The development of natural adhesives derived from non-fossil resources is very important for the future. In this study, by taking sugarcane bagasse as the raw material, without using any synthetic resin but adding some eco-friendly additives (citric acid and sucrose), low density particleboards were successfully developed. The effects of board density and additive contents on the physical and m...
متن کاملPhysical and Mechanical Properties of Particleboard from Bamboo Waste
This research was to evaluate a technical feasibility of making single-layer experimental particleboard panels from bamboo waste (Dendrocalamus asper Backer) by converting bamboo into strips, which are used to make laminated bamboo furniture. Variable factors were density (600, 700 and 800 kg/m) and temperature of condition (25, 40 and 55 C). The experimental panels were tested for their physic...
متن کاملNatural Durability and Performance of Hornbeam Cement Bonded Particleboard
Cement bonded particleboards were manufactured from hornbeam (Carpinus betulus L.) wood particles. Hydration tests were carried out to determine the inhibitory index in order to characterise wood-cement compatibility. The results revealed that the mixture of hornbeam -cement can be classifi ed as moderate inhibition. Two wood: cement ratios were applied in this study, namely 1:3 and 1:4, for th...
متن کاملEffects of the Addition of Citric Acid on Tannin-Sucrose Adhesive and Physical Properties of the Particleboard
The effects of citric acid on the curing properties of tannin-sucrose adhesives and on the physical properties of particleboard utilizing the adhesives were investigated. The citric acid content of tannin-sucrose adhesive was adjusted to 0.4, 1.8, 4.6, 13.8, 20.0, and 33.3%, which corresponded to pH values of the adhesive 40 wt% solution at 3.8, 3.0, 2.5, 2.0, 1.8, and 1.5, respectively. Therma...
متن کاملEvaluation of hydrophilic properties of acrylonitrile/acrylic acid copolymer films dendrigrafted with citric acid
The present study investigates the hydrophilic properties of acrylonitrile/acrylic acid P(AN/AA) copolymer films with various acrylic acid (AA) contents dendrigrafted with citric acid from zero to fourth generation numbers. It was found that the hydrophilicity of the dendrigrafted films was a complicated phenomenon. Various parameters such as intermolecular hydrogen bonding, roughness and activ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Wood Research Journal
سال: 2017
ISSN: 2774-9320,2087-3840
DOI: 10.51850/wrj.2013.4.1.31-35