Characterization and Tensile Fractography of Nano ZrO2 Reinforced Copper-Zinc Alloy Composites
نویسندگان
چکیده
منابع مشابه
Mechanical Characterization and Wear Behavior of Nano TiO2 Particulates Reinforced Al7075 Alloy Composites
In the current research work synthesis, characterization, mechanical and wear behavior of 5 and 10 wt. % of nano TiO2 particulates reinforced Al7075 alloy composites are inspected. The Al7075 alloy and nano TiO2 particle composites were provided by melt stir system. After the preparation, the prepared composites were analyzed by SEM, EDS, and XRD for inquiring the microstr...
متن کاملSynthesis of Nano Alumina Reinforced Magnesium-Alloy Composites
The main aim of this paper was to determine the amount of Al2O3 reinforcement that results into best combination of strength. Magnesium nano composites containing 3.5, 7.0 and 14 volume percentage of Al2O3 were synthesized through powder metallurgy route. Resistance of furnace sintering technique (heating rate: 49°C/min).Micro structural characterization revealed reasonably uniform distribution...
متن کاملFabrication, Characterization and Osteoblast Response of Cobalt-Based Alloy/Nano Bioactive Glass Composites
IIn this work, cobalt-based alloy/ nano bioactive glass (NBG) composites with 10, 15 and 20 wt% NBG were prepared and their bioactivity after immersion in simulated body fluid (SBF) for 1 to 4 weeks was studied. The scanning electron microscopy images of two- step sintered composites revealed a relatively dense microstructure the density of which decreased with the increase in the NBG amount. M...
متن کاملMicrowave-Assisted Sintering of Al–ZrO2 Nano-Composites
Abstract In this project, nano-ZrO2 particles were dispersed in aluminum powder by a Y-shape mixer. The particle size of ZrO2 powder was < 40 nm and the amount of ZrO2 reinforcement varies from 3 to 15%.The mixed powders were compacted .Subsequently the compacted discs were sintered both in the microwave oven and in the conventional muffle furnace .Using microwave –assisted sintering method led...
متن کاملFractography and Mechanical Properties of Urethane Dimethacrylate Dental Composites Reinforced with Glass Nanoparticles
STATEMENT OF PROBLEM Dental resin composites are becoming prevalent in restorative dentistry and have almost replaced amalgam nowadays. Consequently, their mechanical properties and durability are critical. OBJECTIVES The aim of this study was to produce Pyrex glass nano-particles by wet milling process and use them as reinforcement in dental resins for anterior restorations and then examinat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frattura ed Integrità Strutturale
سال: 2019
ISSN: 1971-8993
DOI: 10.3221/igf-esis.48.35