Clarification of Damage Extension Mechanism on 2.25 Cr-1Mo Steel under Creep-Fatigue Loading Condition.
نویسندگان
چکیده
منابع مشابه
Cumulative Fatigue Damage Under stepwise Tension-Compression Loading
Rock structures are subjected to cyclic tension-compression loading due to a blasting, earthquake, traffic and injection-production in underground storage case. Therefore study the fatigue behavior of rock samples under this type of loading is required. In this study, the accumulated fatigue damage for a Green Onyx rock sample which consisted of only one mineral composition with two-step high-l...
متن کاملEffect of Boundary Condition on Pre-Existing Crack Under Fatigue Loading
In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...
متن کاملInterior Fracture Mechanism Analysis and Fatigue Life Prediction of Surface-Hardened Gear Steel under Axial Loading
The interior defect-induced fracture of surface-hardened metallic materials in the long life region has become a key issue on engineering design. In the present study, the axial loading test with fully reversed condition was performed to examine the fatigue property of a surface-carburized low alloy gear steel in the long life region. Results show that this steel represents the duplex S-N (stre...
متن کاملDamage Evolution in Composite Bonded Joints under Fatigue Loading
The fatigue behaviour of single lap bonded joints under fatigue loading was already investigated and a suitable life prediction model was presented and validated [1-2]. The model is based on the actual damage evolution under fatigue load: a crack initiation followed by its propagation up to a critical length [2, 3]. In the present paper the evolution of fatigue damage in single lap joints is ex...
متن کاملStochastic fatigue damage modeling under variable amplitude loading
A general methodology for stochastic fatigue life prediction under variable amplitude loading is proposed in this paper. The methodology combines a nonlinear fatigue damage accumulation rule and a stochastic S–N curve representation technique to achieve this objective. The nonlinear damage accumulation rule proposed in this paper improves the deficiencies inherent in the linear damage accumulat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 2002
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.68.74