Combination of surface nanocrystallization and co-rolling: Creating multilayer nanocrystalline composites
نویسندگان
چکیده
منابع مشابه
Combination of surface nanocrystallization and co-rolling: creating multilayer nanocrystalline composites
This paper presents a combination of the surface mechanical attrition treatment (SMAT) and the corolling process performed at 550 °C. This duplex method leads to the formation of a semi-massive multilayer structure of alternating nanocrystalline layers, transition layers and coarse grain layers. Transmission electron microscope observations correlated with nanoindentation hardness measurements ...
متن کاملSurface alloying of Mg alloys after surface nanocrystallization.
Surface nanocrystallization using a surface mechanical attrition treatment effectively activates the surface of magnesium alloys due to the increase in grain boundary diffusion channels. As a result, the temperature of subsequent surface alloying treatment of pure Mg and AZ91 alloy can be reduced from 430 degrees C to 380 degrees C. Thus, it is possible to combine the surface alloying process w...
متن کاملCreating surfactant nanoparticles for block copolymer composites through surface chemistry.
A simple strategy to tailor the surface of nanoparticles for their specific adsorption to and localization at block copolymer interfaces was explored. Gold nanoparticles coated by a mixture of low molecular weight thiol end-functional polystyrene (PS-SH) (Mn = 1.5 and 3.4 kg/mol) and poly(2-vinylpyridine) homopolymers (P2VP-SH) (Mn = 1.5 and 3.0 kg/mol) were incorporated into a lamellar poly(st...
متن کاملpreparation and characterization of new co-fe and fe-mn nano catalysts using resol phenolic resin and response surface methodology study for fischer-tropsch synthesis
کاتالیزورهای co-fe-resol/sio2و fe-mn-resol/sio2 با استفاده از روش ساده و ارزان قیمت همرسوبی تهیه شدند. از رزین پلیمری resol در فرآیند تهیه کاتالیزور استفاده شد.
Microstructures and mechanical performance of polyelectrolyte/nanocrystalline TiO2 nanolayered composites
Biological materials with hierarchically laminated structures usually exhibit a good synergy between strength and fracture toughness. Here, we show that a bio-inspired (polyelectrolyte (PE)/TiO2)4 nanolayered composite with a thickness ratio of TiO2 and amorphous PE layers of about 1.1 has been prepared successfully on Si substrates by layer-by-layer self-assembly and chemical bath deposition m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scripta Materialia
سال: 2009
ISSN: 1359-6462
DOI: 10.1016/j.scriptamat.2008.08.024