Concentration and temperature dependences of coercive force in Fe-Sm amorphous alloys.
نویسندگان
چکیده
منابع مشابه
Sonochemical preparation of nanosized amorphous Fe-Ni alloys
Nanosized amorphous alloy powders of Fe20Ni80 , Fe40Ni60 , and Fe60Ni40 were prepared by sonochemical decomposition of solutions of volatile organic precursors, Fe~CO!5 and Ni~CO!4 in decalin, under an argon pressure of 100 to 150 kPa at 273 K. Magnetic susceptibility of Fe40Ni60 and Fe60Ni40 indicates blocking temperatures of 35 K and a magnetic particle size of about 6 nm. Thermogravimetric m...
متن کاملEutectic Solidification Limits and Mechanical Properties of Sm-Co-Fe Alloys
Creating a permanent magnet with a higher energy product than existing materials is attractive in order to optimize magnetic performance. The eutectic microstructure of Sm-Co alloys is attractive for magnets since primary rods of the Co-phase can act as a soft magnetic phase in the matrix of the Sm 2 Co 17 hard magnetic phase, forming two-phase magnets. Fe replacement in Sm-Co alloys provides a...
متن کاملPRESSURE EFFECT ON CURIE TEMPERATURE FOR Co1-xBx AMORPHOUS ALLOYS
Pressure effect on Curie temperature, dTc/dp, for amorphous Col-,B, alloys is estimated indirectly from forced volume magnetostriction even in Tc > Tcry. Results estimated indirectly show smaller values compared with those measured directly, and are consistent with thermal expansion. The value of dTc/dp extrapolated to Co agrees with that for crystalline Co.
متن کاملSpin-lattice relaxation in amorphous silicon. Evidence of anomalous temperature dependences
2014 We have investigated the spin-lattice relaxation of localized states in evaporated amorphous silicon films. Temperature and concentration dependences of the relaxation rate have been measured in the temperature range 4.2-290 K. Below 10 K a phonon bottleneck is present. Between 10 and 100 K, a single phonon process predominates. It can be accounted for assuming a significant exchange inter...
متن کاملKINETICS OF -Fe NANOCRYSTALLIZATION IN Fe55Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Abstract: In this research work, crystallization kinetics of Fe55Cr18Mo7B16C4 alloy was evaluated by X-ray diffraction, TEM observations and differential scanning calorimetric tests. In practice, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates. Results showed that a two -step crystallization process occurred in the alloy in which - Fe phas...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1988
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.12.233