Concrete Deterioration under Alternate Action of Carbonation and Sulfate Attack
نویسندگان
چکیده
منابع مشابه
Concrete Carbonation and Chloride Resistance Under Initial Hot Water Curing
Three concrete mix proportions were designed and prepared, respectively, such as fly ash concrete (abbreviated as “FAC”) with 30% fly ash replacement ratio of cement, fly ash, and slag concrete (abbreviated as “FSC”) with each of 20% fly ash and slag replacement ratio and ordinary Portland cement concrete (abbreviated as “OPC”) for the research of carbonation and chloride resistance of concrete...
متن کاملDamage Evolution of Concrete Exposed to Sulfate Attack Under Drying- Wetting Cycles
The damage evolution of concrete subjected to drying-wetting cycles in different concentration of sodium sulfate solution was investigated based on micro and macro-observations. Through the experiment, weight loss, compressive strength loss and the damage layer thickness of concrete were measured after different drying-wetting cycles. The mechanical properties degradation in the damage layer of...
متن کاملModelling and simulation of concrete carbonation: competition of several carbonation reactions
Concrete carbonation, i.e. the reaction of alkaline species (inside the concrete) with atmospheric carbon dioxide, is one of the major physicochemical processes compromising the service life of concrete structures. While the main carbonation reaction is that of calcium hydroxide, other constituents such as calcium silicates or calcium-silcate hydrates in the concrete can also carbonate. Many au...
متن کاملReliability of Reinforced Concrete Girders under Corrosion Attack
Corrosion of reinforcement is a major problem affecting a large number of reinforced concrete structures. At present, most reliability-based design studies of reinforced concrete structures do not consider the effects of corrosion. In this paper, we present a reliability-based approach to the design of reinforced concrete bridge girders that are under corrosion attack. Both reserve and residual...
متن کاملModelling and simulation of concrete carbonation with internal layers
Transport and reaction of carbon dioxide with alkaline species in concrete is modelled by a closed system of ordinary and partial differential equations. Varying porosity and varying external exposure as well as nonlinear reaction rates are taken into account. Proper nondimensionalisation is introduced to pay attention to the different characteristic time and length scales. We emphasise the eff...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Research Journal of Applied Sciences, Engineering and Technology
سال: 2013
ISSN: 2040-7459,2040-7467
DOI: 10.19026/rjaset.6.3584