Conversion of methanol to olefins: Stabilization of nanosized SAPO-34 by hydrothermal treatment

Methanol to olefins: activity and stability of nanosized SAPO-34 molecular sieves and control of selectivity by silicon distribution.

Nano-SAPO-34 molecular sieves synthesized in a microwave environment with 20 nm crystal size showed a longer lifetime than SAPO-34 prepared by the conventional hydrothermal method in the reaction of methanol to olefins. It has been found that silicon distribution strongly affects the lifetime and selectivity. Thus, silicon at the border of the silicon islands gives a higher lifetime and lower C...

The Synthesis of SAPO-34 at Different Crystallization Temperature and its Catalytic Performance for Methanol to Olefins Reaction

Generation of diamondoid hydrocarbons as confined compounds in SAPO-34 catalyst in the conversion of methanol.

Formation of adamantane hydrocarbons and their confinement in SAPO-34 caused the long induction period and the quick catalyst deactivation in methanol conversion. Via ship-in-a-bottle synthesis, adamantane and methyladamantanes could be produced from methanol conversion in the cage of 8-ring SAPO catalysts under very mild reaction conditions.

Influence of the Reaction Temperature on the Nature of the Active and Deactivating Species During Methanol-to-Olefins Conversion over H-SAPO-34

The selectivity toward lower olefins during the methanol-to-olefins conversion over H-SAPO-34 at reaction temperatures between 573 and 773 K has been studied with a combination of operando UV-vis diffuse reflectance spectroscopy and online gas chromatography. It was found that the selectivity toward propylene increases in the temperature range of 573-623 K, while it decreases in the temperature...

Ultrasonic and Microwave Pretreatment for Hydrothermal Synthesis of Nanosized SAPO-34 and Their Catalytic Performance in MTO Reaction (RESEARCH NOTE)

In order to enhance the catalytic performance of SAPO-34 catalyst for the reaction of methanol to olefins (MTO), ultrasonic and microwave-assisted aging method were employed in static hydrothermal method to synthesize nano-sized SAPO-34. The effects of the application of this method on the chemical composition, morphology, surface area and total acidity of SAPO-34 were characterized by XRD, FE-...