Corrosion and Wear Properties of Cr Coating and ZrO2/Cr Bilayer Coating on Zr-4 Alloy
نویسندگان
چکیده
In this study, duplex surface treatments were used to prepare a ZrO2/Cr bilayer coating on zirconium alloy cladding for enhancing the wear and corrosion behaviors. The cross-section morphology of coated Zr-4 was characterized; results show that Cr- ZrO2/Cr-coated samples had similar morphology, more obvious undulates could be observed than pure Cr owing rough plasma electrolytic oxidation coating. Wear electrochemical behavior in 1200 mg/L H3BO3 2.2 LiOH solutions original investigated. test indicated exhibited better resistance alloy. potentiodynamic polarization curves suggest pitting occurred due dual protection PEO layer also investigated under constant load 5 N. reveal resistance, found significantly enhance
منابع مشابه
Direct Electrosynthesis of Polyaniline–Fe2O3 Nanocomposite Coating on Aluminum Alloy 5052 and Its Corrosion Protection Performance
The synthesis of polyaniline- Fe2O3 nanocomposite coating on aluminum Alloy 5052 (AA5052) surface has been investigated by using the galvanostatic method. The anticorrosion performance of polyaniline-Fe2O3 coating was investigated in 3.5% NaCl solution by the open- circuit potential (OCP), Tafel polarization technique and Electrochemical Impedance Spectroscopy (EIS). The corrosion rate of polya...
متن کاملGrowth, corrosion, and wear study of nanocomposite PEO coating in electrolyte containing nickel sulfate
Plasma electrolytic oxidation (PEO) was performed on a 1010 Aluminum alloy. To achieve thenanocomposite structure, Si3N4 nanoparticles were added into the electrolyte. In an alkaline aqueoussuspension (silicate-based), the effect of adding NiSO4 on the applied voltage, microstructure,composition, wear, and corrosion resistance of PEO coatings was investigated using ScanningElectron Microscopy (...
متن کاملGraphene: corrosion-inhibiting coating.
We report the use of atomically thin layers of graphene as a protective coating that inhibits corrosion of underlying metals. Here, we employ electrochemical methods to study the corrosion inhibition of copper and nickel by either growing graphene on these metals, or by mechanically transferring multilayer graphene onto them. Cyclic voltammetry measurements reveal that the graphene coating effe...
متن کاملNanocomposite Coating Based on Thermoplastic Acrylic Resin and Montmorillonite Clay: Preparation and Corrosion Prevention Properties
Different amounts of nanoclay were incorporated into the acrylic resin matrix at 0, 1, 3, and 5 wt.% loadings. The coatings were applied on low carbon steel plates. Optical microscopy, sedimentation test, transmission electron microscopy, and X-ray diffraction were employed to investigate the dispersion of nanoclay in matrix. The corrosion resistance of coatings was evaluated by electrochemical...
متن کاملEnhancement of Adhesion Properties, Corrosion Resistance and Cathodic Disbonding of Mild Steel-Epoxy Coating Systems By Vanadium Conversion Coating
In this study, vanadium conversion coating(VCC) was deposited on the surface of soft-cast steel (St-37). A thermoset coating was enforced on the VCC and blank substrates. The surface was characterized by field emission scanning electron microscope (FE-SEM), elemental mapping of energy dispersive X-ray (EDX) and atomic force microscopy (AFM). The adhesion strength...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Coatings
سال: 2022
ISSN: ['2079-6412']
DOI: https://doi.org/10.3390/coatings12091281