Corrosion Properties Of 1.4512 Ferritic And 1.4404 Austenitic Steels For The Automotive Industry
نویسندگان
چکیده
منابع مشابه
The High Temperature Tensile Properties of Ferritic-martensitic and Austenitic Steels after Irradiation in an 800 Mev Proton Beam
This study examines the effect of tensile test temperatures ranging from 50°C to 600°C on the tensile properties of a modified 9Cr-1Mo ferritic steel (T91) and a 316L stainless steel (SS) after high energy proton irradiation at about 35°C-67°C. After 1-3 dpa, the proton-irradiated T91 steel was tensile tested at temperatures from 50°C to 600°C. It was observed that the yield strength and ultima...
متن کاملDynamic tensile tests on ferritic and austenitic steels with improved testing and measuring technique
For analysing dynamically loaded structures by means of the finite element method a dynamic constitutive material model is necessary to obtain reliable results. For this purpose dynamic tensile tests were performed with the fine grained steel 20MnMoNi 5 5 (A508 CI. 3) and the austenitic steel X6CrNi 18 11'at different velocities. Smooth round bar specimens of different geometries were used. Dis...
متن کاملAtomic-scale decoration for improving the pitting corrosion resistance of austenitic stainless steels
Stainless steels are susceptible to the localized pitting corrosion that leads to a huge loss to our society. Studies in the past decades confirmed that the pitting events generally originate from the local dissolution in MnS inclusions which are more or less ubiquitous in stainless steels. Although a recent study indicated that endogenous MnCr2O4 nano-octahedra within the MnS medium give rise ...
متن کاملThe Influence of Homogenization and Solution Annealing Process on the Microstructure and Mechanical Properties of 1.4470 Ferritic-austenitic Stainless Steel
In the present research, the effect of the homogenization process and annealing temperature were investigated for the 1.4470 ferritic-austenitic stainless steel in the as-cast condition. In this regard, microstructural evolutions, hardness, and impact energy of the steel was evaluated with different heat treatment conditions. The results show that the minimum volume fraction of austenite phase ...
متن کاملGrain Boundary Oxidation and the Chromium- Depletion Theory of Intercrystalline Corrosion of Austenitic Stainless Steels
High temperature microscopy during oxidation of austenitic stainless steels shows that an increased rate of oxidation is found in a narrow zone along grain boundaries where chromium carbides have been precipitated. This lends support to the chromium-depletion theory of intercrystatline corrosion of these steels. Approximate solution of the appropriate diffusion problem shows good agreement with...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: System Safety: Human - Technical Facility - Environment
سال: 2019
ISSN: 2657-5450
DOI: 10.2478/czoto-2019-0095