Crack Initiation and Propagation Fatigue Life of Ultra High-Strength Steel Butt Joints
نویسندگان
چکیده
منابع مشابه
Stress- Corrosion Crack Initiation of High-strength Pipeline Steel in Near-neutral pH Environments
Stress-corrosion cracking (SCC) tests were conducted in the near-neutral pH standard solution, NS4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. Pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...
متن کاملSide Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملFatigue Properties of the Ultra-High Strength Steel TM210A
This paper presents the results of an experiment to investigate the high cycle fatigue properties of the ultra-high strength steel TM210A. A constant amplitude rotating bending fatigue experiment was performed at room temperature at stress ratio R = -1. In order to evaluate the notch effect, the fatigue experiment was carried out upon two sets of specimens, smooth and notched, respectively. In ...
متن کاملNotch fatigue behavior: Metallic glass versus ultra-high strength steel
Studying the effect of notch on the fatigue behavior of structural materials is of significance for the reliability and safety designing of engineering structural components. In this work, we conducted notch fatigue experiments of two high-strength materials, i.e. a Ti32.8Zr30.2Ni5.3Cu9Be22.7 metallic glass (MG) and a 00Ni18Co15Mo8Ti ultra-high strength steel (CM400 UHSS), and compared their no...
متن کاملFatigue Life Assessment of Welded Joints Considering Crack Propagation Based on Hot Spot Stress
In this study, fatigue test and crack propagation analysis of welded joints in ships and offshore structures were performed. The test models have two types of welded joints, T-joint and double plate. Test data is presented in S-N curves obtained by the Hot Spot Stress (HSS) approach. The S-N data for each length of crack were appraised to define the fatigue life of crack initiation and propagat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Sciences
سال: 2019
ISSN: 2076-3417
DOI: 10.3390/app9214590