Cruciform specimens' experimental analysis in ultrasonic fatigue testing
نویسندگان
چکیده
منابع مشابه
Redesigning axial-axial (biaxial) cruciform specimens for very high cycle fatigue ultrasonic testing machines
The necessity to increase performances in terms of lifetime and security in mechanical components or structures is the motivation for intense research in fatigue. Applications range from aeronautics to medical devices. With the development of new materials, there is no longer a fatigue limit in the classical sense, where it was accepted that the fatigue limit is the stress level such that there...
متن کاملThe Design of Cruciform Test Specimens for Planar Biaxial Testing of Fabrics for Inflatable Aerodynamic Decelerators
A preliminary analytical study was conducted to investigate the effects of cruciform test specimen geometries on strain distribution uniformity in the central gage section under biaxial loads. Three distinct specimen geometries were considered while varying the applied displacements in the two orthogonal directions. Two sets of woven fabric material properties found in literature were used to q...
متن کاملFatigue and ultrasonic testing of epoxy-glass composites
Purpose: The purpose of this paper was to find relationship between the degree of strength degradation caused by fatigue and the changes of ultrasonic wave characteristics such as wave velocity and damping coefficient. Design/methodology/approach: Epoxy-glass composites were subjected to oscillatory bending loadings with constant deflection. During fatigue procedure the force needed to achieve ...
متن کاملDifferences in the mechanical properties of calcaneal artificial specimens, fresh frozen specimens, and embalmed specimens in experimental testing.
BACKGROUND Artificial calcanei, fresh-frozen cadaver specimens, and embalmed cadaver specimens were compared in experimental testing under biocompatible loading to clarify the biocompatibility of artificial calcaneal specimens for implant testing. METHODS Two different artificial calcaneal bone models (Sawbone, Pacific Research Laboratories, Vashon, WA, and Synbone, Synbone Inc., Davos, Switz...
متن کاملPrediction of Fatigue Life in Notched Specimens Using Multiaxial Fatigue Criteria
In this research, the effects of notch shape on the fatigue strength of 2024-T3 aluminum alloy notched specimens have been studied using experimental and multiaxial fatigue analysis. For this purpose, four set of specimens with different notch shape were prepared and then fatigue tests were carried out at various cyclic longitudinal load levels. Load controlled fatigue tests of mentioned specim...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Fatigue & Fracture of Engineering Materials & Structures
سال: 2019
ISSN: 8756-758X,1460-2695
DOI: 10.1111/ffe.13041