Damage evolution and rupture time prediction in thermal barrier coatings subjected to cyclic heating and cooling: An acoustic emission method
نویسندگان
چکیده
منابع مشابه
Study of the Frictional Surface Damage Using Acoustic Emission Method
In this study, the change at rubbing surfaces has been investigated experimentally using an acoustic emission signal monitoring system. A steel ring is slipped on the surface of a metallic sheet to simulate frictional conditions. The mechanical disturbances caused by the movement of the ring produce stress waves propagating along the sheet surface. The out of plane displacement of the sheet su...
متن کاملErosion and Foreign Object Damage of Thermal Barrier Coatings
Thermal barrier coating are perceived as an enabling technology to increase the performance of, improve efficiency within, and lower the emissions from, modern gas turbines. To fully utilise this capability one has to be able to accurately predict the life of these coatings under conditions relevant to gas turbine service. This paper addresses the failure of TBC systems as a result of erosion a...
متن کاملThermal Barrier Coatings – Durability Assessment and Life Prediction
Thermal barrier coating (TBC) systems are coating systems containing a metallic bond coat and a ceramic top coat. TBCs are used in gas turbines for thermal insulation and oxidation resistance. Life prediction of TBCs is important as high-temperature exposure degrades the coatings through mechanisms such as thermal fatigue and the formation and growth of thermally grown oxides (TGOs). This thesi...
متن کاملDetection of segmentation cracks in top coat of thermal barrier coatings during plasma spraying by non-contact acoustic emission method
Numerous cracks can be observed in the top coat of thermal barrier coatings (TBCs) deposited by the atmospheric plasma spraying (APS) method. These cracks can be classified into vertical and horizontal ones and they have opposite impact on the properties of TBCs. Vertical cracks reduce the residual stress in the top coat and provide strain tolerance. On the contrary, horizontal cracks trigger d...
متن کاملDamage Energy Evaluation in [55/-55]9 Composite Pipes using Acoustic Emission Method
In this study, the longitudinal and hoop tensile strengths of an industrial ±55° Glass Reinforced Epoxy (GRE) pipe with eighteen layers as well as the associated failure mechanisms are determined. To obtain the longitudinal and hoop tensile strengths values, three specimens are cut from the studied GRE pipe in each direction. A comparison is done between both the strength values, and the fractu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Materialia
سال: 2011
ISSN: 1359-6454
DOI: 10.1016/j.actamat.2011.06.018