Defect formation energy and magnetic properties of aluminum-substituted M-type barium hexaferrite
نویسندگان
چکیده
منابع مشابه
Magnetic and structural properties of M-type barium hexaferrite prepared by co-precipitation
Stoichiometric and single-phase barium hexaferrite (BaM) has been synthesized by co-precipitation and an additional solid state preparative method using high-purity nitrates, oxides and carbonates of iron (III), barium (II) and ammonium hydroxide. The isochronally and isothermally measured permeability and magnetic loss tangents over 1MHz–1GHz in frequency remained moderately constant until a s...
متن کاملMagnetic and microwave absorption properties of barium hexaferrite doped with La3+ and Gd3+
In this paper, BaLaxGdxFe12-2xO19 (x=0.2, 0.4, 0.6 and 0.8) were synthesized via sol-gel auto-combustion method. Fourier transform infrared spectroscopy (FTIR) of samples was represented that the bands at 400 and 500 cm-1 were related to the formation of hexaferrite phase. The (x-ray diffraction) XRD patterns were matched exactly with the structure of barium hexaferrite. (Field emission scanni...
متن کاملStructural, Magnetic and Acetone Sensing Properties of Barium- Calcium Hexaferrite Synthesized by Sol- Gel Auto Combustion Method
In this research, barium calcium hexaferrite (Ba1-xCaxFe12O19 , 0≤x£1) nanoparticles were synthesized through a sol-gel combustion method. The dried gel samples were then calcined at 950ᵒC for 4:30h. The phase and microstructural evolution of calcined samples were investigated by X-ray powder diffraction (XRD) and scanning electron microscopy (SEM), respectively. The results revealed formation ...
متن کاملMagnetic and Structural Properties of Barium Hexaferrite BaFe12O19 from Various Growth Techniques
Barium hexaferrite powder samples with grains in the μm-range were obtained from solid-state sintering, and crystals with sizes up to 5 mm grown from PbO, Na₂CO₃, and BaB₂O₄ fluxes, respectively. Carbonate and borate fluxes provide the largest and structurally best crystals at significantly lower growth temperatures of 1533 K compared to flux-free synthesis (1623 K). The maximum synthesis tempe...
متن کاملThermal annealing effect on the structural and magnetic properties of barium hexaferrite powders
Samples examined in this experimental work were in the form of hexagonal barium ferrite with various temperatures annealing. Barium hexaferrite (BaFe12O19), is of great importance as permanent magnets, particularly for magnetic recording as well as in microwave devices. The variation of the temperatures annealing was found to affect coercivity, mean effective anisotropy field, magnetic viscosit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Computational Condensed Matter
سال: 2014
ISSN: 2352-2143
DOI: 10.1016/j.cocom.2014.11.001