Dephosphorization and Desulfurization of Hot Metal by Lime Based Flux Injection-Oxygen Top Blowing Method
نویسندگان
چکیده
منابع مشابه
The Effect of CaF2 Content in Hot Metal Pretreatment Flux Based on Lime
This research was conducted for the purpose of studying the effect of CaF2 content in the composition of hot metal pretreatment flux, based on lime. It was followed in regards to the importance of fluorine amount decrease in hot metal pretreatment and steel making processes. For this purpose, lime based fluxes including 40, 30, 20 and 10 percent calcium fluoride were prepared and hot metal pret...
متن کاملthe effect of caf2 content in hot metal pretreatment flux based on lime
this research was conducted for the purpose of studying the effect of caf2 content in the composition of hotmetal pretreatment flux, based on lime. it was followed in regards to the importance of fluorine amount decrease in hot metal pretreatment and steel making processes. for this purpose, lime based fluxes including 40, 30, 20 and 10 percent calcium fluoride were prepared and hot metal pretr...
متن کاملThe Effect of Flux type and Oxygen Blowing on Simultaneous Removal of Phosphorus and Sulfur from Molten Iron
This research was conducted to study the effect of lime based Flux with the composition of CaO-20%CaF2-8%FeO on simultaneous removal of phosphorus and Sulfur from hot metal. The effects of Na2O and oxygen blowing were also studied. The experiments were performed using an induction furnace and hot metal produced in Isfahan Steel Company in the temperature range 1350-1450 ºC...
متن کاملthe effect of flux type and oxygen blowing on simultaneous removal of phosphorus and sulfur from molten iron
this research was conducted to study the effect of lime based flux with the composition of cao-20%caf2-8%feo on simultaneous removal of phosphorus and sulfur from hot metal. the effects of na2o and oxygen blowing were also studied. the experiments were performed using an induction furnace and hot metal produced in isfahan steel company in the temperature range 1350-1450 ºc. the results showed t...
متن کاملHot Coal Gas Desulfurization With Manganese-Based Sorbents
The objective of this project is to develop a pellet formulation which is capable of achieving low sulfur partial pressures and a high capacity for sulfur, loaded from a hot fuel gas and which is readily regenerable. Furthermore the pellet must be strong for potential use in a fluidized bed and regenerable over many cycles of loading and regeneration. Regeneration should be in air or oxygen-dep...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1983
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.69.15_1825