Deposition of fluoropolymer coating on stainless steel surface from plasma of glow discharge
نویسندگان
چکیده
Abstract The present work investigates the application of plasma glow discharge to deposit fluoropolymer coatings. Two series experiments were carried out in which influence pressure and current strength on surface coatings morphology during its treatment with was investigated. is investigated by a scanning electron microscope (SEM), water contact angle (WCA) measured. fact that choice significantly affects properties deposited coating established.
منابع مشابه
Factors Affecting Friction Coating on Stainless Steel 304
Low carbon steels are widely used for structural applications because of its ease in fabrication and the moderate strength it posses. However, its pure corrosion resistance at normal atmosphere is a matter of serious concern.
متن کاملCarbon nanotube formation directly on the surface of stainless steel materials by plasma-assisted chemical vapor deposition
We have developed a method for forming carbon nanotubes (CNTs) directly on the surfaces of stainless steel materials that are important industrially. Using plasma-assisted chemical vapor deposition (PCVD), CNTs are formed at comparatively low temperatures, thus avoiding excessive annealing and degradation of the stainless steel. Because the catalytic metals needed for CNT formation are containe...
متن کاملWater Lubrication of Stainless Steel using Reduced Graphene Oxide Coating
Lubrication of mechanical systems using water instead of conventional oil lubricants is extremely attractive from the view of resource conservation and environmental protection. However, insufficient film thickness of water due to low viscosity and chemical reaction of water with metallic materials have been a great obstacle in utilization of water as an effective lubricant. Herein, the frictio...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2021
ISSN: ['1742-6588', '1742-6596']
DOI: https://doi.org/10.1088/1742-6596/2119/1/012125