Deterioration Process of Concrete Exposed to Internal Sulfate Attack
نویسندگان
چکیده
منابع مشابه
Scaling and saturation laws for the expansion of concrete exposed to sulfate attack.
Reinforced concrete structures exposed to aggressive environments often require repair or retrofit even though they were designed to last >50 years. This statement is especially true for structures subjected to sulfate attack. It is critical that fundamental models of life prediction be developed for durability of concrete. Based on experimental results obtained over a 40-year period, scaling a...
متن کاملDamage Evolution of Concrete Exposed to Sulfate Attack Under Drying- Wetting Cycles
The damage evolution of concrete subjected to drying-wetting cycles in different concentration of sodium sulfate solution was investigated based on micro and macro-observations. Through the experiment, weight loss, compressive strength loss and the damage layer thickness of concrete were measured after different drying-wetting cycles. The mechanical properties degradation in the damage layer of...
متن کاملJoint Deterioration in Concrete Pavements
Concrete pavements located in cold climates have been experiencing premature joint deterioration. Entrapment of moisture in the joints saturates the surrounding concrete, rendering it susceptible to freeze–thaw damage. To identify and to isolate the variables that might be causing this localized deterioration, concrete cores were obtained from deteriorated and non-deteriorated sections of US 35...
متن کاملX-ray Microtomography of an Astm C109 Mortar Exposed to Sulfate Attack
X-ray microtomography can be used to generate three-dimensional 5123 images of random materials at a resolution of a few micrometers per voxel. This technique has been used to obtain an image of an ASTM C109 mortar sample that had been exposed to a sodium sulfate solution. The three-dimensional image clearly shows sand grains, cement paste, air voids, cracks, and needle-like trystah growing in ...
متن کاملAn approach for predicting the compressive strength of cement-based materials exposed to sulfate attack
In this paper, a support vector machine (SVM) model which can be used to predict the compressive strength of mortars exposed to sulfate attack was established. An accelerated corrosion test was applied to collect compressive strength data. For predicting the compressive strength of mortars, a total of 638 data samples obtained from experiment was chosen as a dataset to establish a SVM model. Th...