Statistical reliability analyses of two wood plastic composite extrusion processes
Estimates of the reliability of wood plastic composites (WPC) are explored for two industrial extrusion lines. The goal of the paper is to use parametric and non-parametric analyses to examine potential differences in the WPC metrics of reliability for the two extrusion lines that may be helpful for use by the practitioner. A parametric analysis of the extrusion lines reveals some similarities ...
متن کاملEffects of Nano-clay on Biological Resistance of Wood- Plastic Composite against Five Wood-deteriorating Fungi
Effects of nano-clay on weight loss of wood-plastic composites (WPC) by five fungi were studied. Nanoclay particles of 20 to 50 nm size were applied at 2, 4, and 6% WPC of 0,90 g/cm3 density. The white-rot fungi Physisporinus vitreus, Pleurotus ostreatus and Trametes versicolor as well as the brown-rot species Antrodia vaillantii and Coniophora puteana were used. Mass loss tests were conducted ...
متن کاملEffect of Fire Retardants on Surface Roughness and Wettability of Wood Plastic Composite Panels
Surface roughness and wettability of flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) (5, 10, or 15% by weight (wt)) at 50 wt-% content of the wood flour (WF) were investigated. The most common FRs, zinc borate (ZB), magnesium hydroxide (MH), and ammonium polyphosphate (APP), were used in the experiments. The WPC panels were made from dry-blended wood ...
متن کاملPreparation of Wood Plastic Composite with High Density Polyethylene and Bagasse
Abstrac: In this paper, the mechanical properties of high density polyethylene (HDPE grade 3840) produced by Bandare ImamIran, mixed with the wood and bagasse as fillers with 10-50 % w/w have been studied. The maximum tensile strength was observed at 10% w/w of fillers ratio. The elongation, impact strength and fracture energy were decreased with increasing of fillers ratio while the Young modu...
متن کاملDurability of wood plastic composites manufactured from recycled plastic
The influence of accelerated weathering, xenon-arc light and freeze-thaw cycling on wood plastic composites extruded from a recycled plastic was studied. The results showed that, in general, weathering had a stronger impact on samples made from plastic waste compared to a sample made from virgin material. After weathering, the mechanical properties, tensile and flexural, were reduced by 2-30%, ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Waste Resources
سال: 2017
ISSN: 2252-5211
DOI: 10.4172/2252-5211.1000295