ROMP Reactivity of endo- and exo-Dicyclopentadiene
The activation parameters for the ring-opening metathesis polymerization (ROMP) of endo(1) and exo-dicyclopentadiene (2), endo-1,2-dihydrodicylopentadiene (3), and norbornene (4) in the presence of Grubbs’ catalyst were determined using in situ NMR. The exo isomer of DCP was found to be more than an order of magnitude more reactive than the endo isomer. endo-DCP was found to have reactivity sim...
متن کاملThermal properties of ruthenium alkylidene-polymerized dicyclopentadiene
Differential scanning calorimetry (DSC) analysis of ring opening methatesis polymerization (ROMP) derived polydicyclopentadiene (PDCPD) revealed an unexpected thermal behavior. A recurring exothermic signal can be observed in the DSC analysis after an elapsed time period. This exothermic signal was found to be proportional to the resting period and was accompanied by a constant increase in the ...
متن کاملInherently reactive polyHIPE material from dicyclopentadiene.
A simple formulation of a stable high internal phase emulsion of dicyclopentadiene which is cured by using properly selected ring opening metathesis polymerization initiators yields highly porous monolithic materials with paramount mechanical properties and the possibility of easy functionalisation.
متن کاملDevelopment of metal-resin composite restorative material. Part 4. Flexural strength and flexural modulus of metal-resin composite using Ag-In alloy particles as filler.
The flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated. The flexural strength of the experimental metal-resin composites ranged from 65.5 MPa to 91.0 MPa. The flexural strength of the metal-resin composite incre...
متن کاملAdhesion of adhesive resin to dental precious metal alloys. Part II. The relationship between surface structure of Au-In alloys and adhesive ability with 4-META resin.
Adhesion of 4-META to Au-In alloy was improved by adding In equivalent to .15% of Au content. On the basis of the results of Au-In alloys analyzed by XPS, the present study investigated the reason why adhesion of the Au-In alloy was improved. The O 1s spectrum could be separated into three oxygen chemical states, In2O3, chemisorbed H2O, and physisorbed H2O. The amount of chemisorbed H2O decreas...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of The Japan Petroleum Institute
سال: 1984
ISSN: 0582-4664
DOI: 10.1627/jpi1958.27.283