Dopant Concentration Induced Optical Changes in Ca,Eu-α-Sialon
نویسندگان
چکیده
منابع مشابه
Refractory α-SiAlON Containing La2O3
Refractory Y-α-SiAlON with elongated grain morphology was obtained by utilizing La2O3 as a densification aid, which resulted in excellent room-temperature and high-temperature strength. Room-temperature strength of 1000 MPa was achieved when La2O3 was augmented by adding Y2O3 or removing AlN. With only La2O3, a temperature-independent strength of 800–950 MPa was maintained up to 1100°C, then gr...
متن کاملMachinable α-SiAlON/BN Composites
Dense machinable α-SiAlON/BN composites were fabricated by hot-pressing using turbostratic boron nitride (tBN) obtained from nitridation of melamine diborate. The tBN was added to the starting powders, or introduced as a coating that formed in situ on α-Si3N4 carrier powders during nitridation, and was subsequently converted to hexagonal boron nitride (hBN) during hot pressing by solution repre...
متن کاملThe Effect of Powder Mixing Procedures on α- SiAlON
Various procedures of mixing starting powders for hot-pressing α-SiAlON ceramics were studied. They included different milling methods (attrition milling, ball milling, and sonication), liquid medium (water, isopropyl alcohol, and pyridine), and atmospheres (ambient air and nitrogen). These mixing procedures resulted in markedly different densification behavior and fired ceramics. As the powder...
متن کاملOxidation of Ca-α-SiAlON Powders Prepared by Combustion Synthesis
The oxidation of Ca-α-SiAlON synthesized by the combustion synthesis (CS) method with different additives was investigated in air atmosphere using thermogravimetric (TG) analysis in a temperature range from 1453 K to 1653 K. The experimental results indicated that oxidation was controlled by mixed chemical and diffusion steps. The oxidation products by XRD analysis were composed of SiO₂ and CaA...
متن کاملOptical Fiber Drawing and Dopant Transport
Abstract. Optical fibers are made of glass with different refractive indices in the (inner) core and the (outer) cladding regions. The difference in refractive index arises due to a rapid transition in the concentration of a dopant across the boundary between these two regions. Fibers are normally drawn from a heated glass preform, and the different dopant concentrations in the two regions will...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Crystals
سال: 2017
ISSN: 2073-4352
DOI: 10.3390/cryst7110342