Dry Sliding Wear Behavior of B4C and Graphite Particulates Reinforced A356 Alloy Composites
نویسندگان
چکیده
منابع مشابه
Mechanical Characterization and Wear Behavior of Nano TiO2 Particulates Reinforced Al7075 Alloy Composites
In the current research work synthesis, characterization, mechanical and wear behavior of 5 and 10 wt. % of nano TiO2 particulates reinforced Al7075 alloy composites are inspected. The Al7075 alloy and nano TiO2 particle composites were provided by melt stir system. After the preparation, the prepared composites were analyzed by SEM, EDS, and XRD for inquiring the microstr...
متن کاملMicrostructure and Dry-Sliding Wear Behavior of B4C Ceramic Particulate Reinforced Al 5083 Matrix Composite
B4C ceramic particulate–reinforced Al 5083 matrix composite with various B4C content was fabricated successfully via hot-press sintering under Argon atmosphere. B4C particles presented relative high wettability, bonding strength and symmetrical distribution in the Al 5083 matrix. The hardness value, friction coefficient and wear resistance of the composite were higher than those of the Al 5083 ...
متن کاملDry Sliding Wear Behavior of Epoxy-Rubber Dust Composites
Composite pins of rubber dust collected from tyre retreading centres of trucks, cars and buses etc.and epoxy with weight percentages of 10. 15, and 20 % of rubber (weight fractions of 9, 13 and 17 % respectively) have been prepared in house with the help of a split wooden mould. The pins were tested in a pin-on-disc wear monitor to determine the co-efficient of friction and weight losses with v...
متن کاملEFFECTS OF Al-5TI-1B MASTER ALLOY AND HEAT TREATMENT ON THE MICROSTRUCTURE AND DRY SLIDING WEAR BEHAVIOR OF AN Al-12Zn-3Mg-2.5Cu ALLOY
In this study the effect of Al–5Ti–1B grain refiner on the structural characteristics and wear properties of Al–12Zn–3Mg–2.5Cu alloy was investigated. The optimum amount for Ti containing grain refiners was selected as 2 wt.%. T6 heat treatment, (i.e. heating at 460 °C for 1 h before water quenching to room temperature and then aging at 120 °C for 24 h) was applied for all specimens before wear...
متن کاملSoldering of Aluminum Matrix Composites Sicp/a356 and Kovar Alloy
Article history: Received 28.3.2013 Received in revised form 26.4.2013 Accepted 29.4.2013 Aluminum matrix composites containing 55% SiC particle reinforcing phase/SiC reinforcement phase particle and Kovar alloy 4J29 were chosen as the base metals. After nickel plating on the surface of SiCp/Al, two kinds of materials were soldered together by using Zn-Cd-Ag-Cu as the filler metal and ZnCl2 as ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Engineering & Technology
سال: 2018
ISSN: 2227-524X
DOI: 10.14419/ijet.v7i2.23.15330