Ductility Characteristics during Weld Solidification of Al Alloys and Evaluation of Weld Cracking Susceptibility.
نویسندگان
چکیده
منابع مشابه
Weld Metal Ductility: Reduction in Area
It follows from the Chapter 7 that, except for very short gauge lengths, percent elongation is mainly influenced by uniform elongation, and is thus dependent upon the strain-hardening capacity of the matrix. In contrast, reduction in area is more a measure of the deformation required to produce fracture, and its chief contribution arises from the necking process. The work of Groom (1971) illust...
متن کاملStress Corrosion Cracking Susceptibility of 304L Substrate and 308L Weld Metal Exposed to a Salt Spray
304 stainless steels (SS) were considered as the materials for a dry storage canister. In this study, ER (Electrode Rod) 308L was utilized as the filler metal for the groove and overlay welds of a 304L stainless steel substrate, which was prepared via a gas tungsten arc-welding process in multiple passes. The electron backscatter diffraction (EBSD) map was used to identify the inherent microstr...
متن کاملWelding Aluminum Alloy 6061 with Opposing Dual Torch Gtaw Process
Cracking is a major concern in welding aluminum alloys. Although weld solidification cracks can be eliminated through addition of filler alloy, the additives modify the alloy or base-metal constituents and may not always be desirable. High-energy beam processes, such as electron-beam welding, that result in minimal heat input reduce crack sensitivity, but their high cost limits their applicatio...
متن کاملNumerical Modeling of Heat Affected Zone Cracking Tendency during Laser and Hybrid Laser-Arc Welding Processes
A two-dimensional thermal elasto-plastic numerical model is developed by finite element method to analyze and compare the mechanical driving factor for heat affected zone (HAZ) liquation cracking during laser welding and hybrid laser-arc welding techniques. Calculations of transient temperatures and cooling rates are used in conjunction with solidification theory to analyze weld pool characteri...
متن کاملThe Evolution of Cast Microstructures on the HAZ Liquation Cracking of Mar-M004 Weld
The causes of liquation cracking in the heat-affected zone (HAZ) of a cast Mar-M004 superalloy weld were investigated. X-ray diffraction (XRD), electron probe microanalyzer (EPMA), and electron backscatter diffraction (EBSD) were applied to identify the final microconstituents at the solidification boundaries of the cast alloy. Fine borides and lamellar eutectics were present in front of some γ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 1995
ISSN: 0288-4771
DOI: 10.2207/qjjws.13.106