Dynamic microstructural evolution of graphite under displacing irradiation
نویسندگان
چکیده
منابع مشابه
Dynamic Microstructural Evolution of Graphite under Displacing Irradiation
Graphitic materials and graphite composites experience dimensional change when exposed to radiation-induced atomic displacements. This has major implications for current and future technological ranging from nuclear fission reactors to the processing of graphene-silicon hybrid devices. Dimensional change in nuclear graphites is a complex problem involving the filler, binder, porosity, cracks an...
متن کاملFormation and Erosion of Wc under W Irradiation of Graphite
The bombardment of C with 100 keV and 1 MeV W at normal incidence is studied as a function of the incident W fluence experimentally and by computer simulation with the program TRIDYN. Calculated oscillations in the amount of retained W and in the target weight change are confirmed experimentally for 100 keV at room temperature. XPS investigations show W2C formation during ion implantation alrea...
متن کاملEffects of Displacing Radiation on Graphite Observed Using in Situ Transmission Electron Microscopy Original Citation Effects of Displacing Radiation on Graphite Observed Using in Situ Transmission Electron Microscopy
Graphite is used as a moderator and structural component in the United Kingdom’s fleet of Advanced Gas-Cooled Reactors (AGRs) and features in two Generation IV reactor concepts: the Very High Temperature Reactor (VHTR) and the Molten Salt Reactor (MSR). Under the temperature and neutron irradiation conditions of an AGR, nuclear-grade graphite demonstrates significant changes to it mechanical, t...
متن کاملMicrostructural Evolution of X45CrNiW189 Valve Steel During Hot Deformation
The hot compression tests were carried on X45CrNiW189 valve steel (X45) in the temperature range of 1000– 1200 °C and the strain rate range of 0.004 – 0.5 s-1 in order to study the high temperature softening behavior of this steel. For the exact prediction of flow stress, the effective stress-effective strain curves were obtained from experiments under various conditions. On the basis of experi...
متن کاملMicrostructural Characterization of Cobalt-Tungsten Coated Graphite Fibers
The present research concerns an electrodeposited cobalt-tungsten alloy coating on graphite fibers. Annealed and unannealed coated fibers were analyzed by scanning electron microscopy/energy dispersive x-ray spectroscopy (SEM/EDS), x-ray diffraction (XRD), and transmission electron microscopy (TEM). The mole fraction of tungsten in the as-deposited cobalt-tungsten coating was found to be (7.10 ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Carbon
سال: 2014
ISSN: 0008-6223
DOI: 10.1016/j.carbon.2013.11.002