Dynamic Recrystallization of 99.999 mass% Aluminum Single Crystals during Tensile Testing
نویسندگان
چکیده
منابع مشابه
The recrystallization of copper single crystals deformed at 4.2 K
The deformation of copper single crystals at 4.2 K occurs by a sequence of slip, twinning and slip in the twinned structure. Subsequent annealing of the deformed structures obtained at various points at this sequence of deformation permits the detailed nature of the deformed and recrystallized states to be related in a unique fashion. Material recrystallized from structures obtained prior to th...
متن کاملEvidence for Solute Drag during Recrystallization of Aluminum Alloys
Evidence of both solute drag as well as differences in migration mechanisms of certain boundary types has been found for an Al-Zr alloy. In-situ Transmission Electron Microscopy (TEM) annealing experiments coupled with Scanning Transmission Electron Microscopy (STEM) showed a stark contrast between Zr segregation at small and large scales. Specifically, Zr was found to segregate to, as well as ...
متن کاملMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملUltrasonic Monitoring of Recrystallization Textures in Aluminum
The present paper is an attempt to use ultrasonic velocity measurements to characterize the texture of an aluminum-magnesium alloy ( Al 5xxx ) and to compare the results with orientation imaging microscopy ( OIM ) results. The results are characterized in terms of three orientation distribution coefficients ( ODC's ), W400 , W420 , and W440 , each of which describes a particular forming anisotr...
متن کاملAbnormal Plastic Behavior of Fine Grain Mp35n Alloy During Room Temperature Tensile Testing
In this paper, results of an investigation on the strain hardening responses of superalloy MP35N with two average grain sizes of 38 and 1 μm, during room temperature tensile testing are reported. The microstructural evolution of the deformed samples was studied using optical and transmission electron microscopy (TEM) techniques. The strain hardening behavior of the 38 μm material was rather sim...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1998
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.62.1_44