Effect of angle deposition γ on the structural, optical and electrical properties of copper oxide zigzag (+γ, −γ) nanostructures elaborated by glancing angle deposition
نویسندگان
چکیده
منابع مشابه
Designing Nanostructures by Glancing Angle Deposition
Three-dimensional nanostructures can be fabricated by the glancing angle deposition technique. By rotating the substrate in both polar and azimuthal directions, one can fabricate desired nanostructures, such as nanorod arrays with different shapes, nanospring arrays, and even multilayer nanostructures. This method offers a fully three-dimensional control of the nanostructure with additional cap...
متن کاملcontrol of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولNanospring pressure sensors grown by glancing angle deposition.
Arrays of Cr zigzag nanosprings and slanted nanorods, 15-55 nm and 40-80-nm-wide, respectively, were grown on SiO2/Si substrates by glancing angle deposition. The arrays exhibit a reversible change in resistivity upon loading and unloading, by 50% for nanosprings and 5% for nanorods, indicating their potential as pressure sensors. The resistivity drop is due to a compression of nanosprings (by ...
متن کاملTwo-component nanopillar arrays grown by Glancing Angle Deposition
Periodic arrays of 160to 500-nm-wide Si and Cr nanostructures were grown on patterned Si(001) substrates by Glancing Angle Deposition (GLAD). Initial patterning was achieved by colloidal self-assembly of 500-nm-diameter polystyrene and 160-nm-diameter silica microspheres which form, during drying from suspension, close-packed hexagonal arrays. Si deposition onto a monolayer of 500-nmdiameter sp...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Thin Solid Films
سال: 2018
ISSN: 0040-6090
DOI: 10.1016/j.tsf.2018.05.006