Effect of Aqueous Environment on High Cycle and Very-High-Cycle Fatigue Behavior for a Structural Steel
نویسندگان
چکیده
منابع مشابه
Effect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
متن کاملHigh-Cycle, Push–Pull Fatigue Fracture Behavior of High-C, Si–Al-Rich Nanostructured Bainite Steel
The high-cycle, push-pull fatigue fracture behavior of high-C, Si-Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push-pull fatigue limits at 10⁷ cycles were estimated as ...
متن کاملThe Effect of High Cycle Fatigue Damage on Toughness of En8 Grade Steel Part Ii
Fatigue of metals is a subject of practical importance because many components and structures in service are subjected to varying loads and although the average stresses are often low, local concentration of stresses do not reduce the static strength but often lead to failure by fatigue. Micro-crack formation due to fatigue is more in ferritic-pearlitic annealed steel rather than in hardened an...
متن کاملHigh-Cycle Microscopic Corrosion Fatigue Behavior and Life Prediction of 25CrMo Steel Used in Railway Axle
The effects of environmental media on the corrosion fatigue fracture behavior of 25CrMo steel were investigated. The media include air, and a 3.5 wt.% and a 5.0 wt.% NaCl solutions. Experimental results indicate that the media induces the initiation of corrosion fatigue cracks at multiple sites. The multi-cracking sites cause the changes in the crack growth directions, the crack growth rate dur...
متن کاملInfluence of Operating Conditions on High-cycle Fatigue Properties of High Alloyed Steel X20
In this paper, the effect of service temperature and life on high-cycle fatigue properties of base metal, steel X20 CrMoV 12-1, has been analysed. The effect of service conditions has been analysed by testing the new material and material that was in service for 116000 hours. The investigations have included determination of permanent fatigue strength at room and operating temperature. These in...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Key Engineering Materials
سال: 2011
ISSN: 1662-9795
DOI: 10.4028/www.scientific.net/kem.462-463.355