Effect of Bainitic Microstructure on Low-Temperature Toughness of High-Strength API Pipeline Steels
نویسندگان
چکیده
منابع مشابه
High-Strength Bainitic Steels
With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...
متن کاملhigh-strength bainitic steels
with careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thinfilms of stable retained austenite have exhibited impressive combinations of strength and toughness in highsiliconbainitic steels. the silicon suppresses the precipitation of brittle cementite leading to an improvement intoughness. the essential principles governing the optimisation o...
متن کاملThe effects of chemical composition variations on microstructure and mechanical properties of nanostructured, low temperature bainitic steels
Bainitic transformation at low transformation temperatures leads to a microstructure involving fine plates of bainitic ferrite and thin films of retained austenite. This microstructure has shown ultimate tensile strength of about 2.2 GPa, noticeable uniform elongation in the range of 5 to 30%, hardness values of about 600 to 670 HV and impact toughness in the range of 30 to 40 MPa m1/2. With ca...
متن کاملEffect of Mo Content on Microstructure and Property of Low-Carbon Bainitic Steels
In this work, three low-carbon bainitic steels, with different Mo contents, were designed to investigate the effects of Mo addition on microstructure and mechanical properties. Two-step cooling, i.e., initial accelerated cooling and subsequent slow cooling, was used to obtain the desired bainite microstructure. The results show that the product of strength and elongation first increases and the...
متن کاملEffect of Weld Heat Input on Microstructure and Mechanical Properties of Dissimilar Joints of API-B and API-X42 Pipeline Steels
In this study, the effect of welding heat input on microstructure and mechanical properties of dissimilar joints of API-X42 and API-B pipeline steels was investigated. Evaluation of the microstructures showed that increasing the welding heat input decreased acicular ferrite in weld metal microstructure, while amount of Widmanstatten ferrite, polygonal ferrite and grain boundary ferrite increase...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Korean Journal of Metals and Materials
سال: 2020
ISSN: 1738-8228,2288-8241
DOI: 10.3365/kjmm.2020.58.5.293