The Effect of Hot Deformation Parameters on Grain Size Refinement in a Martensitic Stainless Steel
The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligibl...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملStudy on Static Recrystallization Process in Duplex Stainless Steel 2205
Steel 2205 is one of the most famous duplex stainless steels. The microstructure of this steel composed of ferrite and austenite in similar amount. Therefore, in order to improve mechanical properties through microstructure, thermo mechanical processes such as controlled hot rolling and forging should be applied. It is not possible to employ the usual heat treatment. It shows the importance of ...
متن کاملDynamic Recrystallization by Necklace Mechanism During Hot Deformation of 316 Stainless Steel
The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is 316 stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °C with strain rates of 0.01-1s-1. The result shows that at the tempera...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2021
ISSN: 1742-6588,1742-6596
DOI: 10.1088/1742-6596/1820/1/012077